with the aim of identifying failure mechanism in oriented strand boards, failure behavior of wood strands under tensile load was investigated using acoustic emission technique. resinated and unresinated strands were arranged at top, middle and bottom section of the board before pressing. tensile and acoustic emission tests were performed simultaneously on treated and control samples. using tens...

The deformation and failure behavior of an AM60 magnesium alloy was investigated using tensile test on circumferentially notched specimens with different notch radii. The strain and stress triaxiality corresponding to the failure point were evaluated using both analytical and finite element analyses. Combining with systematical observations of the fracture surfaces, it is concluded that deforma...

Blends of polypropylene (PP) and low-density polyethylene (LDPE) may contribute to make recycling more economically attractive. The aim of this work was to make PP/LDPE blends (0/100, 25/75, 50/50, 75/25 and 100/0 w/w) via injection molding carried out under various injection temperatures and to evaluate their tensile and impact properties. The blends yielded tensile stress–strain curves very d...

The tensile properties of sulfonated polyoxadiazoles have been studied as a function of molecular weight and sulfonation level. All sulfonated polyoxadiazoles synthesized through a polycondensation reaction of the hydrazine sulphate salt and a dicarboxylic acid in poly(phosphoric acid) exhibit rigid-ductile behavior with high Young’s modulus (3-4 GPa) and with larger elongations at break (up to...

Polyetherimide (PEI) blends modified by either polycarbonate (PC) or polyethylene terephthalate glycol-modified (PETG) were prepared. The latter modifier (PETG) was an industrial grade widely used for fused deposition modelling (FDM) printing. PEI blends were compared to Ultem 9085, which is the standard PEI grade for FDM printing in advanced applications. All the blends were thoroughly charact...

A Nd:YAG laser was used for joining a pseudoelastic Ti-51.5 at.% Ni shape memory alloy. Tensile tests on sheet metal of 0.5 mm thickness were performed at temperatures of -40°C, +20°C and 1 10°C, representing the martensitic, pseudoelastic and austenitic condition, respectively. Laser-welded specimens exhibited an ultimate tensile strength of about 820 MPa not affected by the test tempefature. ...