In the last decades, the class of Ti-rich TiAl-based intermetallic materials has replaced many contemporary alloys till 900 °C. Due to higher oxidation resistance, 20% lower density and higher (about 150 °C more) operating temperature possibility of Al-rich TiAl alloys over Ti-rich side, phases from the Al-rich region of this alloy system are considered to be highly potential candidates for hig...

The effect of Ti addition on the microstructure and mechanical properties of Cu-15Ni-8Sn alloys was investigated. Optical microscopy (OM), scanning electronic microscopy (SEM), and transmission electron microscopy (TEM) were used to determine grain size and distribution of the second phases in the alloys. The results indicate that the tensile properties of Cu-15Ni-8Sn alloys are improved signif...

In the present work, the oxide layers developed at elevated temperature on three vanadium-free titanium alloys, of interest as implant biomaterials, were studied by Rutherford backscattering spectroscopy, elastic recoil detection analysis, and scanning electron microscopy. The chemical composition of the alloys investigated, in wt%, was Ti–7Nb–6Al, Ti–13Nb–13Zr, and Ti–15Zr–4Nb. Upon oxidation ...

OBJECTIVES Ti, which is biocompatible and resistant to corrosion, is widely used for dental implants, particularly in patients allergic to other materials. However, numerous studies have reported on Ti allergy and the in vitro corrosion of Ti. This study investigated the conditions that promote the elution of Ti ions from Ti implants. METHODS Specimens of commercially pure Ti, pure nickel, a ...

Titanium alloys are known to nucleate an apatite layer when in contact with simulated body fluid. This improves the bioactivity of titanium implants and accelerates osseointegration. Promoting the formation of hydroxyapatite on biocompatible metals is, therefore, a very important topic of biomaterials research. In this paper, the formation of hydroxyapatite (HA) on the near-beta Ti-13Nb-13Zr al...

titanium aluminide and its alloys have been utilized in automotive, aerospace and power industries because of their specific properties such as low density (~ 4 g/cm3), high melting temperature (~ 1460 °c) and excellent high-temperature strength. ti-48al intermetallic compound and its alloys with 1.5, 3 and 5 at.%mn were produced with mechanical alloying of elemental powders for 50 hours. the p...

A major cause of implant failure in skeletal tissues is failure of osseointegration, often due to lack of adhesion of cells to the titanium (Ti) alloy interface. Since arginine-glycine-aspartic acid (RGD)-containing peptides have been shown to regulate osteoblast adhesion, we tested the hypothesis that, bound to a Ti surface, these peptides would promote osteoblasts differentiation, while at th...

This paper presents a study the effect of nose radius (Rz-mm) on cutting force components and temperatures during the machining simulation in an orthogonal cutting process for titanium alloy (Ti-6Al-4V). The cutting process was performed at various nose radiuses (Rz-mm) while the depth of cut (d-mm), feed rate (fmm/tooth) and cutting speed (vc-m/ min) were remained constant. The main cutting fo...

Ti-Hf alloy system forms an α-β isomorphous system and does not form any intermetallic compounds, which is also beneficial for good mechanical properties. The aim of this study was the improvement of mechanical property and biocompatibility by Hf addition to Ti-alloy. Ti-Hf(10, 20, 30 and 40wt%) alloys manufactured by non consumable vacuum arc melting furnace. All the specimens were nanostructu...

The susceptibility to hydrogen absorption and hydrogen thermal desorption of titanium alloys has been investigated in a neutral 2.0% NaF solution at 37 C under various applied cathodic potentials. Ti-0.2Pd, Ti-6Al-4V and Ti-11.3Mo-6.6Zr-4.3Sn alloys absorb hydrogen under less noble potentials than 1:5V, 1:9V and 1:4V versus a saturated calomel electrode, respectively. The amounts of absorbed hy...