Investigation was to study the influence of pulse-impact on microstructure of Liquid-Phase-Pulse-Impact Diffusion Welding (LPPIDW) welded joints of aluminum matrix composite SiCp/A356, SiCp/6061Al, Al2O3p/6061Al. Results showed that under the effect of pulse-impact: 1) the interface state between reinforcement particle (SiC, Al2O3) and matrix was prominently; 2) the initial pernicious contact-s...

Metal matrix composites are the class of composite materials finding vast applications in automotive, aircraft, defense, sports and appliance industries. A horizontal ball mill has been fabricated for milling of aluminum and SiC particles. The change in powder particle morphology during mechanical alloying of Aluminum and SiC powders using horizontal ball mill was studied. Al-SiCp composites wi...

In the present work, the tensile properties and fracture behavior of a 2024Al composite reinforced with 10 vol % SiCp and fabricated via powder thixoforming (PT) were studied at temperatures ranging from 25 ◦C to 300 ◦C with a strain rate of 0.05 s−1, as well as the PT 2024 alloy. The results indicated that the tensile strengths of both the PT materials were all decreased with increasing the te...

Article history: Received 28.3.2013 Received in revised form 26.4.2013 Accepted 29.4.2013 Aluminum matrix composites containing 55% SiC particle reinforcing phase/SiC reinforcement phase particle and Kovar alloy 4J29 were chosen as the base metals. After nickel plating on the surface of SiCp/Al, two kinds of materials were soldered together by using Zn-Cd-Ag-Cu as the filler metal and ZnCl2 as ...

The nano-sized SiCp/Al–Cu composites were successfully fabricated by combining semisolid stirring with ball milling technology. Microstructures were examined by an olympus optical microscope (OM), field emission scanning electron microscope (FESEM) and transmission electron microscope (TEM). Tensile properties were studied at room temperature. The results show that the α-Al dendrites of the com...

The SiC particles (SiCp, mass fraction 30 %) reinforced with the Al-Si-Cu-Mg matrix composite have been prepared using one-way press method, sintering, and hot extrusion. The composite was subjected to solid solution treatment at temperatures of 470 °C, 485 °C, 500 °C, 515 °C, and 530 °C for 4 h. The sample was then subjected to ageing treatment at temperatures of 160 °C and 180 °C during diffe...