In the present study phase transformation of silicon and silica during milling in different atmospheres was investigated. The silicon powder was subjected to high energy ball milling in ammonia (25%) atmosphere. The milled powder was subsequently annealed at 1200 ◦C for 1 hour. In another test a mixture of AlN and amorphous silica (micro silica) was subjected to high energy ball milling. The m...

2012
Tao Ma Shigehito Isobe Yongming Wang Naoyuki Hashimoto Somei Ohnuki

We report a study on the desorption properties, crystallography and chemical state of MgH2 and 1 mol% Nb2O5 ball-milled composites. Desorption temperatures of the composites decreased with increase of ball-milling time. Size of MgH2 crystallites decreased during ball-milling. Reduction of Nb2O5 after ball-milling was confirmed by tracing the chemical state of Nb and was further supported by TEM...

2016
Tan Xing Srikanth Mateti Lu Hua Li Fengxian Ma Aijun Du Yury Gogotsi Ying Chen

Two-dimensional (2D) materials can be produced using ball milling with the help of liquid surfactants or solid exfoliation agents, as ball milling of bulk precursor materials usually produces nanosized particles because of high-energy impacts. Post-milling treatment is thus needed to purify the nanosheets. We show here that nanosheets of graphene, BN, and MoS2 can be produced by ball milling of...

2018
Di Wu Chao Wu Hui Chen Zhenyu Wang Cuiping Yu Ming Du

The effects of ball mill treatment (0, 2, 4, 6, 8, and 10 min) on the physicochemical and digestible properties of scallops (Chlamys farreri) protein (CFP) were investigated. The CFP particle size decreased with increasing ball-milling time. The content of free sulfhydryl (SH) of CFP increased from 13.08 ± 0.25 μmol/g protein to 18.85 ± 0.24 μmol/g protein when the ball-milling time increased f...

ابارشی, مریم,

In the current research, effect of milling on the structure, particle size and morphology of montmorillonite was investigated. For this purpose, the montmorillonite was analyzed by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM). Then the montmorillonite was milled using high energy planetary ball mill at different milling times (1...

Journal: :nanomedicine journal 0
hassan gheisari department of materials engineering, shahreza branch, islamic azad university, shahreza, isfahan, iranسازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (islamic azad university science and research branch) ebrahim karamian advanced materials research center, department of materials engineering, najafabad branch, islamic azad university, najafabad, isfahan, iranسازمان اصلی تایید شده: دانشگاه آزاد اسلامی نجف آباد (islamic azad university of najafabad)

objecttive(s): despite the poor mechanical properties of hydroxyapatite, its unique biological properties leads we think about study on improving its properties rather than completely replacing it with other biomaterials. accordingly, in this study we introduced hydroxyapatite reinforced with hardystonite as a novel bio-nanocompositeand evaluate its in-vitro bioactivity with the aim of developi...

2016
Yong Luo Guang Ran Nanjun Chen Qiang Shen Yaoli Zhang

The microstructural evolution, thermodynamics, and kinetics of Mo (21 wt %) Tm₂O₃ powder mixtures during ball milling were investigated using X-ray diffraction and transmission electron microscopy. Ball milling induced Tm₂O₃ to be decomposed and then dissolved into Mo crystal. After 96 h of ball milling, Tm₂O₃ was dissolved completely and the supersaturated nanocrystalline solid solution of Mo ...

2015
Wen-Liang Zuo Xin Zhao Jie-Fu Xiong Ming Zhang Tong-Yun Zhao Feng-Xia Hu Ji-Rong Sun Bao-Gen Shen

The high coercivity of 26.2 kOe for SmCo5 nanoflakes are obtained by multistep (three steps) surfactant-assisted ball milling. The magnetic properties, phase structure and morphology are studied by VSM, XRD and SEM, respectively. The results demonstrate that the three step ball-milling can keep more complete crystallinity (relatively less defects) during the process of milling compared with one...

Journal: :Physical chemistry chemical physics : PCCP 2016
Chun Kiang Chua Zdeněk Sofer Bahareh Khezri Richard D Webster Martin Pumera

Graphene materials have found applications in a wide range of devices over the past decade. In order to meet the demand for graphene materials, various synthesis methods are constantly being improved or invented. Ball-milling of graphite to obtain graphene materials is one of the many versatile methods to easily obtain bulk quantities. In this work, we show that the graphene materials produced ...

2012
Zongqing Ma Yongchang Liu Liming Yu Qi Cai

The ball milling technique has been successfully applied to the synthesis of various materials such as equilibrium intermetallic phases, amorphous compounds, nanocrystalline materials, or metastable crystalline phases. However, how the phase composition and nanoscale microstructure evolute during ball milling in various materials is still controversial due to the complex mechanism of ball milli...