in comparison to the previous researches, zro2 nanoparticles with higher surface area (85 m2/g) have been synthesized in this research. the as-prepared zro2 nanoparticles by co-precipitation method were characterized with x-ray diffraction (xrd), scanning electron microscopy (sem) and transmission electron microscopy (tem). the surface area of the sample was characterized by bet method. the eff...

in this work, mn ferrite nanopowders were prepared by co-precipitation method and were characterized. phase identification of the nanopowders was performed by x-ray diffraction method and the mean particle size of the nanopowders was calculated by scherrer's formula, using necessary corrections. magnetic parameters of the prepared nanopowders were measured by a vibrating sample magnetomete...

a facile and simple method was proposed to control the size and shape of the mgo nano structures with high surface area in the presence of efficient and cheap templates like peg 200, peg 600, peg 4000 and sorbitol at low temperature within a little time. nano rods and nanoparticles have been achieved by applying these templates and altering other growth parameters. the products were characteriz...

magnetic nanoparticles of cobalt-zinc ferrite (co0.5zn0.5fe2o4) have been synthesized in a homogeneous aqueous solution at room temperature by co-precipitation method without any template and subsequent heat treatment. synthesis of material is confirmed using xrd from the report of single phase polycrystalline ferrite material and also determined lattice constant. atomic absorption spectrophoto...

in this research iron manganese oxide nanocomposites were prepared by co-precipitation, sol-gel and mechanochemical methods by using iron (iii) nitrate, iron (ii) sulfate and manganese (ii) nitrate as starting materials. these nanocomposites were prepared in the presence of various catalyst beds. the polyvinyl pyrrolidon (pvp) was used as a capping agent to control the agglomeration of the nano...

Tin oxide (SnO2)nanoparticles were synthesized by co-precipitation method and the synthesized nanoparticles were annealed at different temperatures for characterization. The powders were investigated with X-ray diffraction, scanning electron microscopy and optical spectroscopy. The structural characterization was carried out by X-ray diffraction which confirms the crystalline nature ...

Nano-structured lanthanum strontium cobalt ferrite, La0.6Sr0.4Co0.2Fe0.8O3 (LSCF), was successfully synthesized via co-precipitation method using metal nitrates as starting materials. Effects of precipitating agent and calcination temperature on the phase composition and morphology of synthesized powders were systematically studied using X-ray diffraction (XRD) and field emission scanning elect...

The synthesis of micro-sized, uniformly distributed Al2O3-15Vol% Ni powders were studied through three step co-precipitation of hydroxides mixtures from proper solution, calcination at air atmosphere and final step of calcined powders in a carbon bed. Al and Ni hydroxide and amorphous phase were first obtained from their salt’s solutions through chemical co-precipitation method by adjusti...

nano-structured lanthanum strontium cobalt ferrite, la0.6sr0.4co0.2fe0.8o3 (lscf), was successfully synthesized via co-precipitation method using metal nitrates as starting materials. effects of precipitating agent and calcination temperature on the phase composition and morphology of synthesized powders were systematically studied using x-ray diffraction (xrd) and field emission scanning elect...

nanostructured zinc oxide (zno) materials have received considerable interest from scientists due to their remarkable performance in electronics, optics and photonics. zno nanoparticles were synthesized by co-precipitation method. zno nanoparticles were synthesized using zn(no3)3 and k2co3 precursors. the structure of the obtained product was confirmed by the powder x-ray diffraction (xrd) anal...