In this study, the pitting type of corrosion growth characteristics, fatigue crack initiation and propagation behavior; axial fatigue tests were carried out on precipitation hardened martensitic Custom 450 steel in the air and 3.5wt% NaCl solution. Using the ratio of the depth to the half-width of the pits; (a/c)= 1.5±0.2 the corrosion pit depth growth law was obtained as a function of stress a...

The corrosion fatigue crack growth characteristics of small (>35pm) surface and corner cracks in aluminum alloy 7075 is established. The early stage of crack growth is studied by performing in situ long focal length microscope (500X) crack length measurements in laboratory air and 1% NaCl environments. To quantify the “small crack effect” in the corrosive environment, the corrosion fatigue crac...

The effects of environmental media on the corrosion fatigue fracture behavior of 25CrMo steel were investigated. The media include air, and a 3.5 wt.% and a 5.0 wt.% NaCl solutions. Experimental results indicate that the media induces the initiation of corrosion fatigue cracks at multiple sites. The multi-cracking sites cause the changes in the crack growth directions, the crack growth rate dur...

Fatigue crack growth behavior of AZ61 magnesium alloy was investigated in low humidity (55% relative humidity) and 3.5% NaCl spray environments under various stress ratios. Fatigue crack growth rates became higher with increasing load ratio for both environments. However, the results of fatigue crack growth test under 3.5% NaCl spray environment showed lower fatigue crack propagation rate compa...

In this paper, a Paris law-based model is presented whereby crack propagation occurs under cyclic loading in air (fatigue) and in an aggressive environment (corrosion-fatigue) for the case of corner cracks (with a wide range of aspect ratios in the matter of the initial cracks) in finite-thickness plates of 316L austenitic stainless steel subjected to tension, bending, or combined (tension + be...

The corrosion fatigue performance of high-strength bolt was studied. Based on the fracture mechanics theory and the Gerberich-Chen formula, the high-strength bolt corrosion fracture crack model and the fatigue life model were established. The high-strength bolt crack depth and the fatigue life under corrosion environment were quantitatively analyzed. The factors affecting high-strength bolt cor...

This paper evaluates the effects of microbiologically influenced corrosion (MIC) on fatigue-crack growth of candidate materials useful in expanding bio-ethanol usage, including a storage-tank steel (ASTM A36) and two pipeline steels (API 5L X52 and X70). The microbiological species sampled and cultivated from an ethanol fuel production stream are responsible for both acetic acid and hydrogen su...

Single-crystal aluminas are being considered for use in the manufacture of prosthetic heart valves. To characterize such materials for biomedical application, subcritical crack growth by stress corrosion (static fatigue) and by cyclic fatigue has been examined in sapphire along (1100) planes in 24 degrees C humid air and 37 degrees C Ringer's solution (the latter as a simulated physiological en...

In this work, the effects of loading condition and corrosion solution on the corrosion fatigue behavior of smooth steel wire were discussed. The results of polarization curves and weight loss curves showed that the corrosion of steel wire in acid solution was more severe than that in neutral and alkaline solutions. With the extension of immersion time in acid solution, the cathodic reaction of ...

The development and current state-of-the-art in fracture mechanics in relation to studies of environment-enhanced fatigue-crack growth (corrosion fatigue) and fatigue-crack growth per se are reviewed. Patterns of response of materials to different loading and environmental conditions are considered in terms of the probable mechanisms for environmental embrittlement. The usefulness of the fractu...