Scratches are deleterious to precision optics because they can obscure and modulate incident laser light, which will increase the probability of damage to optical components. We here imitated the generation of brittle and ductile scratches during polishing process and endeavored to find out the possible influence of scratches on laser induced damage. Brittle scratches can be induced by spiking ...

this work is an attempt towards employing ductile damage criterion and finite elementsimulations for prediction of fracture initiation and evolution in deep drawing of copper/stainlesssteel clad sheets. the material mechanical properties and ductile damage parameters weredetermined through standard and notched tensile tests. the effect of some important processparameters on damage evolution wer...

To accurately predict ductile failures of new advanced metals, continuum damage models (CDMs) require experimental determination of material-specific damage parameter(s). While various experimental techniques are being used to determine these damage parameter(s), possible systematic errors due to methodological differences in damage definition have yet to be fully revealed. With the aim of find...

Fracturing by ductile damage occurs quite naturally in metal forming processes, and ductile fracture of strain-softening alloy, here 42CrMo steel, cannot be evaluated through simple procedures such as tension testing. Under these circumstances, it is very significant and economical to find a way to evaluate the ductile fracture criteria (DFC) and identify the relationships between damage evolut...

The continuum mechanic simulation of micro-structural damage process is important in the study of ductile fracture mechanics. In this paper, the continuum damage mechanics model formulation proposed by Lematire has been validated against ductile damage evolution experimentally measured in A533B-C1 steel under stress triaxiality conditions. First, a &#10procedure to identify the model parameters...

The continuum mechanic simulation of micro-structural damage process is important in the study of ductile fracture mechanics. In this paper, the continuum damage mechanics model formulation proposed by Lematire has been validated against ductile damage evolution experimentally measured in A533B-C1 steel under stress triaxiality conditions. First, a procedure to identify the model parameters f...

Stress fractures, a painful injury, are caused by excessive fatigue in bone. This study on damage accumulation in bone sought to determine if the Palmgren-Miner rule (PMR), a well-known linear damage accumulation hypothesis, is predictive of fatigue failure in bone. An electromagnetic shaker apparatus was constructed to conduct cyclic and variable amplitude tests on bovine bone specimens. Three...

Mechanical degradation and resultant capacity fade in high-capacity electrode materials critically hinder their use in high-performance rechargeable batteries. Despite tremendous efforts devoted to the study of the electro-chemo-mechanical behaviours of high-capacity electrode materials, their fracture properties and mechanisms remain largely unknown. Here we report a nanomechanical study on th...

in the present research, damage mechanisms during room temperature uniaxial tensile testing of two different modern high strength dual phase steels,dp780 and dp980, were studied. detailed microstructural characterization of the strained and sectioned samples was performed by scanning electron microscopy (sem). the results revealed that interface decohesion, especially at the triple junctions of...

A viscoplastic deformation model considering material damage is used to predict hot tear formation in a permanent mold magnesium alloy casting. The simulation model calculates the solid deformation and ductile damage. The viscoplastic constitutive theory accounts for temperature dependent properties and includes creep and isotropic hardening. Ductile damage theory is used to find mechanically i...