abstract statement of problem: mechanical strength and durability of dental composites are the main topics studied in this field of science today. this study examined fumed silica-based composite as a strong and durable restorative material through flexural and cycling test methods.     objectives: the purpose of this study was to evaluate the effect of silanization, ageing, cycling and hybridi...

STATEMENT OF THE PROBLEM Composite resin may be used in different temperatures; it is crucial to determine the effect of temperature on mechanical properties of nanohybrid and silorane-based composite. PURPOSE This in vitro study compared the flexural strength and modulus of elasticity of nanohybrid and silorane-based resin composite, at 4˚C, room temperature (25˚C), and 45˚C. MATERIALS AND...

The flexural strength and flexural modulus of an experimental metal-resin composite, which used Ag-In alloy particle as the filler, were evaluated. The effect of acid treatment and heat treatment on the Ag-In alloy particle was investigated. The flexural strength of the experimental metal-resin composites ranged from 65.5 MPa to 91.0 MPa. The flexural strength of the metal-resin composite incre...

background: flexural strength of prosthesis made with dental composite resin materials plays an important role in their survival. the aim of this study was investigating the effect of nanoclay fillers and poly (methyl methacrylate)-grafted (pmma-grafted) nanoclay fillers loading on the flexural strength of fiber-reinforced composites (frcs). materials and methods: standard frc bars (2 × 2 × 25 ...

in this research, a braiding-pultrusion production line is developed by modifying a conventional textile maypole braiding machine and adding it to a pultrusion line for production of braid-pultruded (bp) composite rods. in order to evaluate the mechanical properties of bp rods and study the effect of some braiding parameters, they were produced with different braid roving linear densities and b...

in the present research work, the flexural modulus and strength of glass fiber-epoxy resin and carbon fiber-epoxy resin composites have been enhanced through fiber tension during curing of the polymeric resin. this study showed that the tension applied on the fibers increased the flexural modulus of the glass-epoxy composites up to 12% and the flexural strength up to 19%. the flexural modulus a...

The purpose of this study was to evaluate the mechanical behavior of three composites with nanoparticles Filtek Z350 XT (3M ESPE), Esthet X (Dentsply), Grandio (Voco) in enamel and body shades (A2) trough nanohardness, elastic modulus, compressive strength test, flexural strength test, diametral tensile strength, flexural modulus, weight filler content and Knoop microhardness. One sample of eac...

OBJECTIVES To measure the flexural strengths and moduli of endodontic post materials and to assess the effect on the calculated flexural properties of varying the diameter/length (D/L) ratio of three-point bend test samples. METHODS Three-point bend testing of samples of 2mm diameter metal and fiber-reinforced composite (FRC) rods was carried out and the mechanical properties calculated at su...

BACKGROUND The use of composites in dental restoration has been commonly criticized, due to their underwhelming mechanical properties. This problem may be solved partially by preheating. The present research aims to determine the effect of preheating on the mechanical properties of two different classes of composites. MATERIAL AND METHODS A Silorane-based (Silorane) and a Methacrylate-based (...

PURPOSE The aim of this study was to clarify the effect of addition of glass fibers and titanium dioxide nanoparticles to the conventional acrylic resin. The tested parameters were monomer release, deflection at fracture, flexural strength, flexural modulus, and toughness. The modified acrylic resin groups were compared to the conventional unmodified and high impact types. The correlation betwe...