the aim of this study was to investigate the sol gel synthesis of ha/fa nanoparticles and the possible formation of tcp phase or unstoichiometric calcium deficient hydroxyapatite (cdha) from the precursors with a ca/p ratio of 1.62. in order to prepare the sol, the solutions of triethyl phosphite, ammonium fluoride and calcium nitrate in ethanol were used respectively as p, f and ca precursors....

in this investigation, fluor-hydroxyapatite (fha) film was deposited on a titanium substrate by sol-gel method. triethyl phosphite, ammonium fluoride and calcium nitrate in ethanol solutions were used respectively as p, f and ca precursors. typical apatite structures were obtained for all coatings after dipping and subsequent heat treatment at 550, 700 and 800 ºc, the coating layers were invest...

      In this investigation, fluor-hydroxyapatite (FHA) film was deposited on a titanium substrate by sol-gel method. Triethyl phosphite, ammonium fluoride and calcium nitrate in ethanol solutions were used respectively as P, F and Ca precursors. Typical apatite structures were obtained for all coatings after dipping and subsequent heat treatment at 550, 700 and 800 ºC, the coating layers were ...

Fluoride has a specific affinity for hydroxyapatite bone Ca10(PO4)6(OH)2. It lists the hydroxyl ions of hydroxyapatite crystals converting it into Fluor apatite, which entails a change of the physical characteristics of the crystals. Fluorapatite crystals are quick dimension "a" crystal, increased crystallinity and a reduced dissolve. Increased solubility of fluorapatite is the main cause of ch...

In this study, new nano-fluor-hydroxyapatite (nFHA)/polyurethane composite scaffolds were fabricated for potential use in bone tissue engineering. Polyester urethane samples were synthesized from polycaprolactone, hexamethylene diisocyanate, and 1,4-butanediol as chain extender. Nano fluor-hydroxyapatite (nFHA) was successfully synthesized by sol-gel method. The solid-liquid phase separation an...

Hydroxyapatite (HA), fluor-hydroxyapatite (FHA) with varying levels of fluoride ion substitution and fluorapatite (FA) were synthesised by the sol-gel method as possible implant coating or bone-grafting materials. Calcium nitrate and triethyl phosphite were used as precursors under an ethanol-water based solution. Different amounts of ammonium fluoride were incorporated for the preparation of t...

The aim of this study was to investigate the sol gel synthesis of HA/FA nanoparticles and the possible formation of TCP phase or unstoichiometric calcium deficient hydroxyapatite (CDHA) from the precursors with a Ca/P ratio of 1.62. In order to prepare the sol, the solutions of Triethyl phosphite, ammonium fluoride and calcium nitrate in ethanol were used respectively as P, F and Ca precursors....