photocatalytic degradation of diazinon from marine source using tio2/sio2 thin layer coated on glass
tio2 photo catalyst was prepared in presence of nano sio2 and hydroxy propyl cellulose (hpc) by sol gel method with titanium tetra isopropoxide (ttip) as titanium precursor. additional effect of hpc in preparation of nano catalyst, and photo catalyst properties measured and characterized by ft-ir, ft-raman and sem. the catalyst size and structural properties of the film were determined by .-ray...
nano zno/ montmorillonite composite were prepared by sol gel method under ultrasonic irradiation from directly mixing montmorillonite nano clay into zinc gel. the zn(ch3coo)2.2h2o and montmorillonite nano clay was used as precursor. the zinc acetate was dissolved in di water and, nh3 (aq) solution was dropped into the zinc solution until ph 9 consequently the zinc gel was produced. the montmori...
Photocatalytic Degradation of Diazinon From Marine Source Using TiO2/SiO2 Thin Layer Coated on Glass
TiO2 photo catalyst was prepared in presence of nano SiO2 and Hydroxy Propyl Cellulose (HPC) by sol gel method with Titanium Tetra IsoproPoxide (TTIP) as titanium precursor. Additional effect of HPC in preparation of nano catalyst, and photo catalyst properties measured and characterized by FT-IR, FT-Raman and SEM. The catalyst size and structural properties of the film were determined by .-Ray...
in recent years, the effects of heterogeneous catalysts for the oxidation of organic and inorganic pollutants in industrial wastewaters are spread. traditionally, these reactions are usually carried out using suspensions of photo-catalysts such as tio2. a chemical method including ticl4, al(no3)3, ethanol amine, ethyl acetoacetate and aqueous ammonia were used for the fabrication of tio2-al2o3 ...
nickel doped tio2 nano particles (1% w/w) were prepared and immobilized on nax zeolite and after characterization by x-ray diffraction (xrd) and scanning electron microscopy (sem) used as photo catalyts for degradation of orange g. the xrd patterns show that the supported tio2 are crystallized in anatase form and the intensity of the zeolite peaks decreases with the increase of tio2 loading. sc...
BACKGROUND Photo-degradation of organic contaminants into non-hazardous mineral compounds is emerging as a strategy to purify water and environment. Tremendous research is being done using direct solar light for these purposes. In this paper we report on optimum conditions for complete mineralization of aqueous methyl orange using lab-prepared ZnO nanopowder catalyst under simulated solar light...
In recent years, the effects of heterogeneous catalysts for the oxidation of organic and inorganic pollutants in industrial wastewaters are spread. Traditionally, these reactions are usually carried out using suspensions of photo-catalysts such as TiO2. A chemical method including TiCl4, Al(NO3)3, ethanol amine, ethyl acetoacetate and aqueous ammonia were used for the fabrication of TiO2-Al2O3 ...
zno and mn-zno nano powders were prepared by the sol-gel auto combustion method. the products were characterized by x-ray diffraction (xrd), energy dispersive analysis of x-ray (edx) and scanning electron microscopy (sem). structural and morphological properties of nano particles were investigated and the average crystalline size of zno and mn-doped zno was obtained 44 and 51 nm, respectively. ...
In this research, Zn2SiO4 as a support and MnFe2O4 as a main photo-catalyst were individually syn-thesized and MnFe2O4 was fixed on Zn2SiO4 with solid state dispersion method. MnFe2O4 nano pho-to-catalyst was synthesized by co-precipitation method and reflux condition for 12 hours at 85°C in the presence of urea. For identification of catalysts Fourier-transform infrared (FTIR) sp...
Nickel doped TiO2nano particles (1% w/w) were prepared and immobilized on NaX zeolite and after characterization by X-ray diffraction and scanning electron microscopy used as photo catalyts for degradation of orange G. The X-ray diffraction patterns show that the supported TiO2 are crystallized in anatase form and the intensity of the zeolite peaks decreases with the incre...