In this work, we study the lithiation behaviours of both porous silicon (Si) nanoparticles and porous Si nanowires by in situ and ex situ transmission electron microscopy (TEM) and compare them with solid Si nanoparticles and nanowires. The in situ TEM observation reveals that the critical fracture diameter of porous Si particles reaches up to 1.52 μm, which is much larger than the previously r...

Porous collagen scaffold is integrated with surface activated PLLA nanoparticles fabricated by lyophilizing and crosslinking via EDC treatment. In order to prepare surface-modified PLLA nanoparticles, PLLA was firstly grafted with poly (acrylic acid) (PAA) through surface-initiated polymerization of acrylic acid. Nanoparticles of average diameter 316 nm and zeta potential -39.88 mV were obtaine...

Fluorescence imaging is one of the most versatile and widely used visualization methods in biomedical research. However, tissue autofluorescence is a major obstacle confounding interpretation of in vivo fluorescence images. The unusually long emission lifetime (5-13 μs) of photoluminescent porous silicon nanoparticles can allow the time-gated imaging of tissues in vivo, completely eliminating s...

Porous TiO2 were assembled by evaporating or refluxing TiO2 colloid, which was obtained by dispersing the TiO2 nanoparticles with a crystallite size (d XRD) of 3.2 nm into water or ethanol without any additives. Porous transparent bulk TiO2 was obtained by evaporating the TiO2-C2H5OH colloid at room temperature for 2 weeks, while porous TiO2 nanospheres were assembled by refluxing the TiO2-H2O ...

We demonstrate the one-step synthesis of a silica-gold nanocomposite by simultaneous hydrolysis and reduction of gold chloride. The aminophenyl group was used as a reducing agent, and the trimethoxy silane group acts a precursor for the formation of silica. The porous gold nanoparticles were formed by etching out the silica-gold nanocomposite by hydrofluoric acid. The electron diffraction of po...

We report on a novel slow dynamics of polymer xerogels, aerogels, and nanocomposite aerogels with iron oxide nanoparticles, as revealed by X-ray photon correlation spectroscopy. The polymer aerogel and its nanocomposite aerogels, which are porous in nature, exhibit hyper-diffusive dynamics at room temperature. In contrast, non-porous polymer xerogels exhibit an absence of this peculiar dynamics...

Biofilms are a common constituent of the subsurface and are known to influence contaminant transport; however only a few studies to date have addressed microbial controls on nanoparticle mobility in porous media. The impact of a 3-day Pantoea agglomerans biofilm on the mobility of zinc oxide (ZnO) nanoparticles was studied in column experiments containing sand and glass beads at near-neutral pH...

Gold nanoparticles encapsulated in porous carbon spheres with high surface areas (~800 m(2) g(-1)) have been synthesized by ultrasonic spray pyrolysis (USP). The porous carbon-encapsulated gold nanoparticles exhibit excellent catalytic activity toward the reductions of both hydrophilic and hydrophobic nitroaromatics.

For controlled release and targeted delivery of curcumin in an aqueous medium a method of encapsulating curcumin and magnetic nanoparticles inside porous silica matrix has been developed. Curcumin and superparamagnetic nanoparticles are loaded inside porous silica in a single process. The graphic shows the TEM image of microtomed sample of Fe(3)O(4) particles surrounded by a silica matrix.

The electrophoretic deposition of nanoporous TiO2 layers allows us to investigate separately the influence of sintering temperature, porosity, and conformal surface coatings on the effective diffusion coefficient Deff of excess electrons in porous layers. Photocurrent transients were measured to obtain Deff in nanoporous TiO2 layers immersed in aqueous electrolyte. The applied treatments contro...