Colloidal silica bonded refractory castables have been developed recently. It was found that colloidal silica is one of the best binders can substitute other binders such as cement in No Cement Castable (NCC) and Ultra Low Cement Castable (ULCC) refractories. Also composition of colloidal silica with appropriate additives resulted in a gel form which makes the initial strength. Moreover, the na...

TiO2-SiO2 core-shell particles include of monodisperse silica core and nanostructured titania shell were synthesized by a multi-step coating process. The monodisperse silica spheres were synthesized by Stöber method and titania shell was obtained of a colloidal sol prepared by a hydrolysis–condensation reaction. The titania sol was deposited on monodisperse silica spheres by a multi-step coatin...

We have described a new and promising strategy for the fabrication of composite and porous photonic crystal microparticles that combines the self-assembly of colloidal particles with photolithography techniques. We fabricated silica/SU-8 composite microparticles with photonic bandgaps via four steps: (1) deposition of the silica colloidal crystals on the photoresist, (2) embedding of the colloi...

this study is focused on synthesis of nano-colloidal silica via alkaline water glass solution. sodium ions of water glass were removed by cation exchanging in a resin column to obtain the silicic acid which was titrated to the solution of sodium silicate. concentration of the colloidal silica and ph value of the solutions were controlled using different concentrations of alkaline sodium silicat...

Self-assembly of colloidal particles into colloidal films has many actual and potential applications. While various strategies have been developed to direct the assembly of colloidal particles, fabrication of crack-free and transferrable colloidal film with controllable crystal structures still remains a major challenge. Here we show a centrifugation-assisted assembly of colloidal silica sphere...

Anisotropic colloidal building blocks are quite attractive as they enable the self-assembly towards new materials with designated hierarchical structures. Although many advances have been achieved in colloidal synthetic methodology, synthesis of colloidal rings with low polydispersity and on a large scale remains a challenge. To address this issue we introduce a new site-selective growth strate...

This study is focused on synthesis of nano-colloidal silica via alkaline water glass solution. Sodium ions of water glass were removed by cation exchanging in a resin column to obtain the silicic acid which was titrated to the solution of sodium silicate. Concentration of the colloidal silica and pH value of the solutions were controlled using different concentrations of alkaline sodium silicat...

We investigated the origin of birefringence in colloidal films of spherical silica particles. Although each particle is optically isotropic in shape, colloidal films formed by drop drying demonstrated birefringence. While periodic particle structures were observed in silica colloidal films, no regular pattern was found in blended films of silica and latex particles. However, since both films sh...

The net charge of a colloidal particle was controlled using light and a new photocleavable self-assembled monolayer (SAM). The SAM contained a terminal ammonium group and a centrally located carboxylic acid group that was masked with an ortho-nitrobenzyl functionality. Once exposed to UV light, the 2-nitrobenzyl group was cleaved, therefore transforming the colloidal particle from a net positiv...

This study is focused on synthesis of nano-colloidal silica via alkaline water glass solution. Sodium ions of water glass were removed by cation exchanging in a resin column to obtain the silicic acid which was titrated to the solution of sodium silicate. Concentration of the colloidal silica and pH value of the solutions were controlled using different concentrations of alkaline sodium silicat...