In this work, the investigation of wave absorption, phase formation, crystal structure and magnetic properties of SrFe12O19 hexa-ferrites nanoparticles that synthesized by co-precipitation using a microwave heating system and polyaniline-SrFe12O19 was carried out by using a combination of vector network analyser (VNA), X-ray diffraction (XRD), scanning electron microscopy (SEM), and Fourier tra...

Thermal decomposition of nickel hexa(format0) fetrate(DQ decahydrate i.e. Ni3ve(HC00)s]2. 10H,O has been studied upto 913 K in static air atmosphere employing TG,DTG,DTApSC,XRD$!SR, Mossbauer and f i r e d spectroscopic techniques. Dehydration occurs in two stages in the temperature range of 348-423 K. Immediately &r the removal of the last water molecule, the anhydrous complex undergoes decomp...

Magnetic powder of Sr-ferrite was prepared by conventional and sol-gel auto-combustion methods. In conventional method, strontium carbonate and ferric oxide powders were mixed together and then mixture was calcined. In sol-gel auto-combustion method, a solution containing strontium nitrate, ferric nitrate and citric acid was heated until the combustion took place automatically; then, as-burnt p...

In this paper, strontium ferrite (SrO.6Fe2O3) was synthesized by the sol-gel auto-combustion process. The thermal behavior of powder obtained from self-propagating combustion of initial gel was evaluated by simultaneous differential thermal analysis (DTA) and thermo gravimetric (TG), from room temperature to 1200°C. The as-burnt powder was calcined at various temperatures from 700-900°C to achi...

The influence of La substitution on the structure, magnetic and electric properties of Sr hexaferrite is examined in isotropic and anisotropic samples. High quality hard ferrite is obtained with 1 weight % of La substitution ( for SiOz doping samples as well).

Introduction Magnetic oxide nanomaterials, including iron oxide (Fe3O4 and γ-Fe2O3), spinel ferrites (MFe2O4; M=Mn, Zn, Cr, Ni, or Co) and hexagonal ferrite (MFe12O19, M=Ba and Sr) are attracting much attention due to their wide application potentials in advanced magnets, electronic devices, information storage, magnetic resonance imaging (MRI), and drug-delivery technology [1-6]. Hence, the sy...

Microwave ferrites require high coercivity for their use as microwave absorbers. Strontium hexaferrite is one of the best material due to its magnetic properties , high coercivity, large unilateral magnetic anisotropy and very low cost in comparison to others make it suitable for the use as microwave components specifically microwave absorber .Strontium nano hexa ferrites were successfully synt...

Sodium hexa-titanate (Na(2)Ti(6)O(13)) nanofibers, which have microporous tunnels, were prepared by heating sodium tri-titanate nanofibers with a layered structure at 573 K. The void section of the tunnels consist of eight linked TiO(6) octahedra, having a quasi-rectangular shape and the sodium ions located in these tunnel micropores are exchangeable. The exchange of these sodium ions with diva...