The purpose of this study was to compare the known behavior of hydrogen embrittled high-strength steel to the characteristics of environmentallyinduced stress corrosion failure where hydrogen is continuously generated at the specimen surface. The incubation time for the initiation of slow crack growth was accelerated by prestressing for a fixed time below the lower critical limit. These results...

−The 2-chlorophenol (2-CP) was oxidized in a continuous anti-corrosive supercritical water system. The variation of decomposition efficiency by the corrosion of zirconium 702 was also studied at the variation of feed concentration and reaction time. According to AES depth profile, the oxygen penetration depth to zirconium was not proportional to the exposure time. It might stem from the formati...

In this study, the ability of lithium nitrite and amino alcohol inhibitors to provide corrosion protection to reinforcing steel was investigated. Two types of specimens-reinforcing steel and a reinforced concrete prism that were exposed to chloride ion levels resembling the chloride attack environment-were prepared. An autoclave accelerated corrosion test was then conducted. The variables teste...

Pitting corrosion is localized accelerated dissolution of metal that occurs as a result of a breakdown of the otherwise protective passive film on the metal surface. This paper provides an overview of the critical factors influencing the pitting corrosion of metals. The phenomenology of pitting corrosion is discussed, including the effects of alloy composition, environment, potential, and tempe...

The high temperature corrosion behavior of sputtered nanocrystalline K38 coating with and without yttrium addition under mixed molten salt film in air was investigated. Accelerated corrosion occurred on the coating without yttrium (Y) addition locally after 60 h exposure at 900 °C, which resulted in negative weight gain in kinetics. A uniform and protective alumina scale formed on surface of th...

Durability of reinforced concrete with respect to corrosion of reinforcement is one of the major aspects to be considered in the management of civil infrastructure systems. An accelerated laboratory test method developed at SERC where the concrete specimen containing rebar is subjected to polarization under a constant voltage in a sodium chloride solution. It is found that the current response ...

Reinforced concrete beams are normally designed as under-reinforced to provide ductile behaviour at failure i.e. the tensile moment of resistance, Mt(0), is less than the moment of resistance of the compressive zone, Mc. Since it is well established that the steel in reinforced concrete beams is prone to corrosion, the residual flexural strength is normally the main concern of asset managers. H...

In the present paper the corrosion properties of structured sheet metals were investigated. The aim of this work is to determinate the influence of the structuring process on the corrosion resistance of sheet metals. For this purpose, these sheets were examined by accelerated tests in corrosion chamber. The investigation was carried out using salt spray test. The experiment was conducted for th...

Metallic coatings using thermal spraying techniques are widely applied to structural steels to protect infrastructure against corrosion and improve durability of the associated structures for longer service life. The thermal sprayed metallic coatings consisting of various metals, although have higher corrosion resistance, will still corrode in a long run and may also subject to corrosion induce...