Plastic encapsulated microcircuits with aluminum triple track structures were exposed to mixed flowing gas conditions to simulate and accelerate possible environments during long-term storage. No increase in resistance was measured and no corrosion products were observed after 800 h of accelerated exposure. Further experimentation indicated that chloride gas reacts with surface moisture in micr...
Microbes in marine biofilms aggregated into clusters and increased the production of extracellular polymeric substances (EPS), by over 100% in some cases, when the seawater media containing toxic metals and chemicals, such as Cd(II), Cu(II), Pb(II), Zn(II), AI(III), Cr(III), glutaraldehyde, and phenol. The formation of microbial cluster and the increased production of EPS, which contained 84-92...
Bacteria biofilm formation on metals is well-known, while biofilm architecture varies under different conditions. To date, few studies have determined the possible contribution to corrosion of titanium made by biofilm architecture. We investigated the interaction between the oral Streptococcus sanguis biofilm architecture and its influence on titanium corrosion in enriched artificial saliva usi...
Acoustic emission (AE) technique is used for monitoring and evaluating the influence of corrosion on the structural behaviour of steel reinforced concrete (RC) beams under three-point flexure test. In this study, steel corrosion was accelerated by electro-chemical method utilising a direct current (DC) power supply and 5% sodium chloride (NaCl) solution. The steel corrosion that was induced int...
There is a wide range of engineering systems where either the efficiency, the cost, or the reliability and lifetime is limited by high temperature corrosion processes. This includes gas turbines, boilers of various kinds, coal gasifiers, reformers and catalytic regenerators in the petrochemical industry, and heat exchangers and heat recovery systems of many kinds. The issues can largely be sepa...
Hydrostatic pressure effects on pitting initiation and propagation in X70 steel are investigated by evaluating metastable pitting probability using electrochemical methods and immersion corrosion tests in containing chlorine ion solution. Potentiodynamic tests indicated that hydrostatic pressure can decrease the breakdown potential and lead to a reduced transpassivity region. Metastable test re...
304 stainless steel was tested under the media without Sulfate-reducing bacteria (SRB) and with SRB. The corrosion behaviors of 304 stainless steel in SRB and without SRB medium were studied by measuring the open circuit potential, the polarization curves and electrochemical impedance Spectrum,weight loss measurements to get the changes of fore-and-aft corrosion fouling. The open circuit potent...
Corrosion cracking of reinforced concrete caused by chloride salt is one of the main determinants of structure durability. Monitoring the entire process of concrete corrosion cracking is critical for assessing the remaining life of the structure and determining if maintenance is needed. Fiber Bragg Grating (FBG) sensing technology is extensively developed in photoelectric monitoring technology ...
A study has been presented on the effects of intrinsic mechanical parameters, such as surface stress, surface elastic modulus, surface porosity, permeability and grain size on the corrosion failure of nanocomposite coatings. A set of mechano-electrochemical equations was developed by combining the popular Butler-Volmer and Duhem expressions to analyze the direct influence of mechanical paramete...