in this study , the physical and mechanical properties of polypropylene composites reinforced with bagasse alkaline-sulfite-anthraquinone, soda-anthraqouinone, monoethanolamine-anthraquinone chemical pulps and mechanical pulp (cmp) known as pulp-plastic compostes (ppc) were investigated and the results were compared among ppcs and with polypropylene composites reinforced with bagasse flour know...

Aalto University, P.O. Box 11000, FI-00076 Aalto www.aalto.fi Author Jouko Lehto Name of the doctoral dissertation Reinforcement ability of mechanical pulp fibres Publisher School of Chemical Technology Unit Department of Forest Products Technology Series Aalto University publication series DOCTORAL DISSERTATIONS 47/2011 Field of research Paper and Printing Research Manuscript submitted 2 Novem...

EXPERIMENTAL A softwood (mainly spruce) bleached kraft pulp (SWBKP), and a hardwood (eucalyptus) bleached kraft pulp (HWBKP) were refined in a PFI mill to 470 and 490 ml CSF freeness, respectively. Three grades of commercial aspen high-yield pulp (325/85, 325/83, 250/80) were obtained from Tembec Inc., without further refining treatment. The properties of the pulp samples are listed in Table I....

Basic fiber properties can be classified into four categories: Size distribution, shape, structure of the cell wall and the fiber surface. This approach was used when long fiber fractions separated from 10 different mechanical pulps and unrefined and refined chemical pulp samples were compared in order to shed light on the different reinforcing abilities of chemical and mechanical pulp fibers. ...

Canola straw can be used as a raw material for the production of chemimechanical pulp (CMP). In this work, chemimechanical pulp was first produced from canola straw, and then the bleaching performance of the produced chemimechanical pulp was investigated under different conditions (dosages of NaOH and Na2SO3, time, and temperature). The results showed that the yield of chemical pretreatment in ...

Three selected alkali-based organosolv pulps (alkali-sulfite-anthraquinone-methanol (ASAM), alkali-anthraquinone-methanol (organocell) and ethanol-soda) from agrofibre crop giant reed (Arundo donax L.) were bleached by an ozone-based TCF (totally chlorine- free) bleaching sequence AZE(R)QP (where A is an acidic pulp pre-treatment, Z is an ozone stage, (E(R)) is an alkaline extraction in the pre...

Extraction of hemicelluloses prior to pulping and conversion of the extracted hemicelluloses to other bioproducts could provide additional revenue to traditional pulp and paper industries. The effect of hemicelluloses pre-extraction with a hydrothermal (HT) process on Pinus radiata chemimechanical pulp (CMP) properties was investigated in this study. The HT extraction resulted in a release of 7...

Residual lignin carbohydrate complexes (RLCC) were isolated enzymatically from spruce and pine pulp. The RLCCs contained 4.9–9.4% carbohydrates, with an enrichment of galactose and arabinose compared to the original pulp samples. The main carbohydrate units present in all studied RLCCs were 4-substituted xylose, 4-, 3and 3,6-substituted galactose, 4-substituted glucose and 4 and 4,6-substituted...