Polymethylmethacrylate (PMMA)/ceria composite fibres were synthesized by using a sequential combination of polymer electrospinning, spray-coating with a sol, and a final calcination step to yield microstructured ceria tubes, which are composed of nanocrystalline ceria particles. The PMMA template is removed from the organic/inorganic hybrid material by radio frequency (rf) plasma etching follow...

We have demonstrated the synthesis of γ-Fe2O3 nano-particles through a facile and novel calcination process in the air. There is no pH regulation, gas atmosphere, additive, centrifugation or other complicated procedures during the preparing process. A detailed formation process of the nano-particles is proposed, and DMF as a polar solvent may slower the reaction process of calcination. The stru...

In this work, hydrochloric acid is used to remove iron impurities in the bauxite ore contained in the diasporite mineral located in the Sari region. The bauxite ore was calcined at different temperatures and times, and then dissolved in a hydrochloric acid solution. After determining the optimum calcination conditions in 1 h at 900 °C, the response surface methodology (RSM) with four factors in...

Ceria-titania solutions with compositions of Ce0.9Ti0.1O2 and Ce0.8Ti0.2O2 were prepared by the citric-acid (Pechini) method and characterized using x-ray diffraction (XRD) for structure, coulometric titration for redox thermodynamics, and water-gas-shift (WGS) reaction rates. Following calcination at 973 K, XRD suggests that the mixed oxides exist as single-phase, fluorite structures, although...

The structure of the mesoporous silica SBA-16 has been interrogated by careful elimination of the organic templating agent using ozone treatment. It is shown that the as-synthesised material consists of large cages connected by very narrow, ca. 7 Å, windows. These windows open up to about 20 Å following a calcination treatment that suggests that the functionality of SBA-16 could be changed mark...

Three quarters of the world’s phosphate deposits are of sedimentary origin and 75%–80% of those include carbonate gangue. In this study, carbonate sedimentary phosphate deposits of the Lar Mountains of southwest Iran are studied. These deposits consist mainly of calcite, fluorapatite, quartz, kaolinite and illite, with an average P2O5 grade of 9%–10% (low-grade). Various pre-processing and proc...

The composites graphite/ZnO were prepared using calcination method. Zinc chloride (ZnCl2) and sodium carbonate (Na2CO3) were used for synthesis of zinc oxide (ZnO), whereas micromilled and natural graphite were used as the matrix for ZnO nanoparticles growing. During the reaction of ZnCl2 with saturated aqueous solution of Na2CO3 new compound Na2Zn3(CO3)4•(H2O)3 originates. During the calcinati...

The effects of chemical composition and preparation conditions, especially calcination atmosphere, water content and oxygen content on the catalytic performances of MoVTeNbO mixed oxide catalyst system for the selective oxidation of propane to acrylic acid have been investigated and discussed. Among the catalysts studied, the Mo1.0V0.3Te0.23Nb0.12O catalyst calcined in inert atmosphere under a ...

Bimetallic catalysts (Co:Mo ≈ 2:1 in atomic ratio) were prepared on quartz substrates from metal acetate solutions using a procedure of dip coating, followed by calcination and reduction. High-purity single-walled carbon nanotubes (SWNTs) 1–2 nm in diameter were grown densely (~1.0×10 17 m-2) and vertically on these substrates during an alcohol catalytic chemical vapor deposition process. To cl...