The Corrosion inhibition of an inhibitor namely Copper complex of 1-(8-hydroxy quinolin-2-yl-methyl) thiourea (Cu-HTF) which controls the corrosion of mild steel immersed in an aqueous solution containing 60 ppm Cl has been investigated through electrochemical and mass loss method. The formulation consisting of 60 ppm of Cl and 50 ppm of Cu-HTF offers good inhibition efficiency of 78 %. Polariz...

Water wetting is a crucial issue in carbon dioxide (CO2) corrosion of multiphase flow pipelines made from mild steel. This study demonstrates the use of a novel benchtop apparatus, a horizontal rotating cylinder, to study the effect of water wetting on CO2 corrosion of mild steel in two-phase flow. The setup is similar to a standard rotating cylinder except for its horizontal orientation and th...

The electrochemical behavior of mild steel in bicarbonate solution at different dissolved oxygen (DO) concentrations and immersion times has been studied under dynamic conditions using electrochemical techniques. The results show that both DO and immersion times influence the morphology of the corrosion products. In comparative tests, the corrosion rate was systematically found to be lower in s...

The influence of the acid extract of peel of Cucurbita maxima (PCM) on the corrosion of mild steel in 1N H2SO4 was investigated by weight loss, polarization and impedance methods and SEM analysis. The inhibition efficiency increases with extract concentration and immersion period. Weight loss and corrosion rates of mild steel decreased as the concentration of inhibitor increased. The results sh...

The corrosion inhibition of mild steel in 1M H2SO4 by polyvinyl pyrrolidone (PVP) and the synergistic effect of iodide ions were investigated using weight loss and hydrogen evolution methods in the temperature range of 30 – 60 o C. The corrosion rates of mild steel decreased with the increasing concentration of PVP, while the inhibition efficiency (%I) increased. The inhibition efficiency of PV...

The corrosion inhibition of mild steel in 0.5 M H2SO4 solution has been investigated using electrochemical methods, X-ray diffraction (XRD) and scanning electron microscope (SEM). The adsorption and inhibition action of acid corrosion of mild steel using cetyltrimethylammonium bromide (CTABr) and different halides (NaCl, NaBr and NaI) has shown synergetic effect. The results showed that the pro...

Abstract—This paper presents a fully Lagrangian coupled Fluid-Structure Interaction (FSI) solver for simulations of fluid-structure interactions, which is based on the Moving Particle Semi-implicit (MPS) method to solve the governing equations corresponding to incompressible flows as well as elastic structures. The developed solver is verified by reproducing the high velocity impact loads of de...

The influence of [Fe]-hydrogenase from Clostridium acetobutylicum was studied on the anaerobic corrosion of mild steel. Two short-circuited mild steel electrodes were exposed to the same solution and hydrogenase was retained on the surface of only one electrode thanks to a dialysis membrane. The galvanic current and the electrode potential were measured as a function of time in order to monitor...

In this research, mesoporous silica was applied as the host of corrosion inhibitor (molybdate). The loaded mesoporous silica was dispersed in an epoxy matrix. The composite was then coated on the mild steel plate. Results showed that the corrosion resistance of the scratched epoxy/mesoporous silica loaded by molybdate was better than the one without molybdate or neat epoxy. On the other hand, E...