thermal barrier coatings (tbcs) are used to provide thermal insulation to the hot section components of gas turbines in order to enhance the operating temperature and turbine efficiency. hot corrosion and thermal shocks are the main destructive factors in tbcs which comes as a result of oxygen and molten salt diffusion into the coating. in this thesis atmospheric plasma spraying was used to dep...
Specimens of the SA508-IV reactor pressure vessel (RPV) steel, containing 3.26 wt. % Ni and just 0.041 wt. % Cu, were irradiated at 290 ◦C to different displacement per atom (dpa) with 3.5 MeV Fe ions (Fe2+). Microstructure observation and nano-indentation hardness measurements were carried out. The Continuous Stiffness Measurement (CSM) of nano-indentation was used to obtain the indentation de...
Additions of high modulus nano particles to Aluminum alloys offer the potential to develop a lightweight composite with high mechanical properties. It is extremely difficult to disperse nano-sized ceramic particles uniformly in molten metal. In order to investigate the effect of nano-alumina on the microstructure and mechanical properties of composite, a new method was used in stir casting to a...
introduction: resin composites are an important part of restorative treatment in modern dentistry. there are many trademarks available in iran market and physico-chemical properties of many of these resin composites are not evaluated yet. this study was carried out to evaluate the physico-chemical properties of four available resin composites and also to assess the effect of aging on their prop...
INTRODUCTION Dental caries is a major public health problem, and Streptococcus mutans is considered the main causal agent of dental caries. This study aimed to compare the effect of three re-mineralizing materials: resin infiltrant, fluoride varnish, and nano-hydroxy apatite paste on the surface hardness and adhesion of Streptococcus mutans as noninvasive treatments for initial enamel lesions. ...
in this study, aluminum (al) matrix reinforced with micro-particles (30 µm) and nano-particles (50 nm) boron carbide (b4c) were used to prepare al-2.5%wt., b4c nano-composite and micro-composite, respectively, using mechanical alloying method. the mixed powders were mechanically milled at 5, 10, 15 and 20 hrs. the xrd results indicated that the crystallite sizes of both the micro-composite and ...
background: the aim of this study was to compare the effects of conventional acid etching and laser etching on the nano-mechanical properties of the dental enamel using nano-indentation test. materials and methods: in this experimental in vitro study, buccal surfaces of 10 premolars were divided into three regions. one of the regions was etched with 37% phosphoric acid and another etched with e...
Nano-scratch and nano-indentation were used to determine hardness, elastic modulus, adhesion, friction and wear resistance of chromium oxide coatings in air and in water. The friction coefficient is higher in water, compared to air, and it increases with the applied normal load, although there are no obvious differences in hardness and elastic modulus in air vs. water. A higher normal load incr...
OBJECTIVE Erosion of tooth surface is attributed to recent shift in diet pattern and frequent use of beverages. The aim of this research was to evaluate the effects of different beverages on surface topography and hardness of nano-filled composite material. METHODS Sixty flat disc shaped resin composite samples were fabricated and placed in distilled water for 24 hours. After 24 hours test sa...
0026-2714/$ see front matter 2010 Elsevier Ltd. A doi:10.1016/j.microrel.2010.06.013 * Corresponding author. Tel.: +852 2788 7130; fax: E-mail address: [email protected] (Y.C. Chan Nano-sized, nonreacting, noncoarsening Al2O3 particles have been incorporated into eutectic Sn–Zn solder alloys to investigate the microstructure, hardness and shear strength on Au/Ni metallized Cu pads ball grid...