Zirconium diboride ceramics with and without carbon boron carbide nanopowder additives were prepared by ball milling ZrB2 grinding media pressureless sintering. Additions of up to 1 wt% nano-B4C 0.5 C made the powder. The materials then sintered between 1800 2300 °C for 90 360 min in an Ar/10H2 atmosphere. After sintering at 2200 min, densities ranged from 88.3 90.7% 0–1.0% addition. Carbon add...
Two processes to sinter monolithic hexagonal Barium AluminoSilicate (BAS) are compared in this study: Spark Plasma Sintering (SPS) and a new Ultra-Fast Pressureless (UFPS) technology developed by Galtenco Solutions®. For both, BAS was sintered its thermal stability range (between 1590 °C 1760 °C). Results demonstrate that it is only possible manufacture small parts (15 mm diameter/ 5 height) of...
The aim of the present research was to fabricate and study crystal structure and phase composition of Bi5FeTi3O15 (BTFO) ceramics exhibiting Aurivillius type structure. By means of simultaneous thermal analysis and X-ray diffraction analysis the process of synthesis of BTFO ceramics has been studied. Mixed oxide method followed by pressureless sintering was used for ceramics preparation. Three ...
Dielectric materials with high permittivity are strongly demanded for various technological applications. While polarization inherently exists in ferroelectric barium titanate (BaTiO3), its high permittivity can only be achieved by chemical and/or structural modification. Here, we report the room-temperature colossal permittivity (~760,000) obtained in xNd: BaTiO3 (x = 0.5 mol%) ceramics derive...
نمودار تعداد نتایج جستجو در هر سال
با کلیک روی نمودار نتایج را به سال انتشار فیلتر کنید