Fatigue crack growth was investigated in a 001 1⁄2 oriented single crystal specimen, made of a Ni-based superalloy, Haynes 230. Crack propagation was characterized with digital image correlation: crack closure, measured by analyzing the relative displacements of crack flanks, showed closure levels much lower than polycrystal alloys. Reversed plastic zones were calculated from regressed stress i...

The mechanisms of fatigue-crack propagation in ceramics and intermetallics are examined through a comparison of cyclic crack-growth behavior in ductile and brittle materials. Crack growth is considered to be a mutual competition between intrinsic mechanisms of crack advance ahead of the crack tip, which promote crack growth, and extrinsic mechanisms of crack-tip shielding behind the tip, which ...

We have developed an experiment to study the propagation of laboratory synthesized fatigue cracks under various controlled conditions during Sonic IR inspection. The experiment provides for good repeatability in testing. The parameters of interest include the initial crack length, load history (stress intensity and load ratio) during crack generation, geometry of the crack, material and also th...

this study investigates propagation of mode i crack in b70 pre-stressed concrete sleepers by fracture mechanics approach. a new experimental analysis is done for notched b70 pre-stressed concrete sleepers with replica test and image analysis. a scanning electron microscope test (sem) and an image analysis are applied for the replica test in order to determine crack length and crack mouth openin...

In order to improve upon continuum models for understanding the origins of ductile versus brittle response in materials, an accurate assessment of the stress fields near a crack tip must be developed. Existing continuum models have considered the crack tip to be perfectly sharp in order to use convenient analytical solutions for the stress fields around the crack tip. Numerous experimental obse...

This paper presents a study of generalized enrichment functions for three-dimensional curved crack fronts. Two coordinate systems used in the definition of singular curved crack front enrichment functions are analyzed. In the first one, a set of Cartesian coordinate systems defined along the crack front is used. In the second case, the geometry of the crack front is approximated by a set of cur...

An extensive experimental study of indentation and crack arrest statistics is presented for four different brittle materials (alumina, silicon carbide, silicon nitride, glass). Evidence is given that the crack length statistics is described by a universal (i.e., material independent) distribution. The latter directly derives from results obtained when modeling crack propagation as a depinning p...

The cracked Brazilian disc (CBD) specimen is widely used in order to determine mode-I/II and mixed-mode fracture toughness of a rock medium. In this study, the stress intensity factor (SIF) on the crack-tip in this specimen is calculated for various geometrical crack conditions using the extended-finite element method (X-FEM). This method is based upon the finite element method (FEM). In this m...

The fracture of restored teeth is a significant obstacle to lifelong oral health. Recent studies suggest that fatigue cracks originate at flaws introduced during cavity preparation and that fatigue crack growth is a principle cause of restored tooth fractures. In this study, the rate of fatigue crack growth in bovine dentin was estimated under mode I cyclic loading. Double cantilever beam (DCB)...

The saturation-strip model for piezoelectric crack is re-examined in a permeable environment to analyze fracture toughness of a piezoelectric ceramic. In this study, a permeable crack is modeled as a vanishing thin but finite rectangular slit with surface charge deposited along crack surfaces. This permeable saturation crack model reveals that there exists a possible leaky mode for electrical f...