The use of fly ash is not only in harmony with the concept of sustainable development, but also beneficial to some mechanical properties of concrete. This paper discusses steel corrosion rate time-changing law in concrete with different replacing ratios of low calcium fly ash(10%~30%) and the microcosmic characteristic of concrete-steel interface. The steel corrosion rate was tested by linear p...

The electrochemical corrosion behaviour of mild steel embedded in concrete, and partially immersed in 0.2M H2SO4, was studied in this investigation at ambient temperature by potential monitoring technique. The experimental work was performed with a digital multimeter and a Cu/CuSO4 electrode (CSE) as the reference electrode. Extracts of carica papaya leaves and sodium nitrite (NaNO2) in differe...

Corrosion inhibition behavior of Ascorbic acid (AA) vitamin C and Thiamine (Th) vitamin B1 on mild steel corrosion in 0.5 M HCl was investigated at various immersion times. The electrochemical characteristics of mild steel in absence and presence of the inhibitors were verified by the cyclic voltammetry method. The protective properties of the passive film were acquired by electrochemical imped...

In the present paper, changes in mechanical properties of Portland cement-based mortars due to the addition of carbon nanotubes (CNT) and corrosion of embedded steel rebars in CNT cement pastes are reported. Bending strength, compression strength, porosity and density of mortars were determined and related to the CNT dosages. CNT cement paste specimens were exposed to carbonation and chloride a...

The resistance and susceptibility of austenitic stainless steel, Type 304, exposed to strong tetraoxosulphate (VI) acids (2 and 5 M concentrations) contaminated with sodium chloride at ambient temperatures was investigated by gravimetric and metallographic/scanning electron microscopy surface characterization methods. Scanning electron microscope (SEM) was used to examine and characterize the t...

Results from the international cooperative programme on effects on materials including historic and cultural monuments are presented from the period 1987-2014 and include pollution data (SO₂, NO₂, O₃, HNO₃ and PM10), corrosion data (carbon steel, weathering steel, zinc, copper, aluminium and limestone) and data on the soiling of modern glass for nineteen industrial, urban and rural test sites i...

The applications of stainless steel are one of the most reliable solutions in concrete structures to reduce chloride-induced corrosion problems and increase the structures service life, however, due to high prices of nickel, especially in many civil engineering projects, the austenitic stainless steel is replaced by the ferritic stainless steels. Compared with austenite stainless steel, the fer...

aisi 304l austenitic stainless steel with different grain sizes of 0.5 -12 μm was obtained through the martensiticprocess. corrosion behavior of different samples was investigated in a 0.5m hcl solution using open circuitpotential, potentiodynamic polarization and electrochemical impedance spectroscopy tests. also, the correlationbetween the grain size and pitting corrosion resistance was asses...

The chemical degradation of alloy components in sulfur-containing environments is a major concern in oil and gas production. This paper discusses the effect of elemental sulfur and its simplest anion, sulfide, on the corrosion of Cr-Mo alloy steel at pH 2 and 5 during 10, 20 and 30 h immersion in two different solutions. 4130 Cr-Mo alloy steel is widely used as tubing and tubular components in ...

The carbon dioxide corrosion electrochemistry of mild steel has been studied in the presence of high CO2 partial pressures and acetic acid (HAc). Potentiodynamic sweeps, linear polarization resistance (LPR) and weight loss (WL) experiments have been conducted to investigate the effects of flow velocity, CO2 partial pressure, and acetic acid concentration on the corrosion rate of mild steel. Ele...