During the last 10 years, with the development of nanocrystalline films of very high surface area, the photosensitization of wide-bandgap semiconductors, such as TiO2, by adsorbed dyes has become more realistic for solar-cell applications. In a porous film consisting of nanometer-sized TiO2 particles, the effective surface area can be enhanced 1000-fold, thus making light absorption efficient e...

A wet-chemical method for increasing the number of quantum dots (QDs) per unit surface area of TiO2 was developed. High density QD surface coating was induced by a surface charge controlled SILAR method, which led to a sixfold increase in photocurrent density from 2.15 mA cm(-2) to 15.03 mA cm(-2) in a QD-sensitized solar cell based on a Hg-doped PbS sensitized 2.4 μm-thick TiO2 film.

a  commercial  ti-nanoxide  was  deposited  on  in-doped  sno2 (ito) polymer  substrates by  tape casting  technique with different thicknesses  (7,  14  and  36μm)  to  be  used  as  photoelectrode  in flexible  dye-sensitized  solar  cells  (dsscs).  ruthenium  dye  was adsorbed on each tio2 film for 24 h. the resulting photoelectrodes were used to form flexible dsscs in combination with elec...

Hollow hemispherical titanium dioxide (TiO2) aggregates (HHTAs) consisting of P25 TiO2 nanocrystallites were prepared by a coaxial electrospray method and applied to dyesensitized solar cells (DSCs). Although the photoelectrode film constructed with HHTAs possesses an internal surface area lower than that of one with dispersed P25 TiO2 nanocrystallites and thus achieves less dye adsorption, it ...

Conductive and transparent multilayer thin films consisting of three alternating layers (TiO2/Ag/SiO2, TAS) have been fabricated for applications as transparent conducting oxides. Metal oxide and metal layers were prepared by electron-beam evaporation with ion-assisted deposition, and the optical and electrical properties of the resulting films as well as their energy bounding characteristics a...

In sputtering deposition process of TiO2, metal Ti or sintered TiO2 target is used as deposition source. In this study, we have compared the characteristic of target materials. When TiO2 target was used, stoichiometric TiO2 films was deposited under the Ar atmosphere containing 1.0% of oxygen. The highest sputtering rate under this atmosphere was 3.9nm/min at 3.4W/cm2. But, sintered TiO2 target...

Titanium dioxide sTiO2, with the rutile structured was grown on s0001d oriented GaN and s0001d Al0.33Ga0.67N/GaN heterostructure field effect transistor sHFETd structures by molecular beam epitaxy. X-ray diffraction showed s100dTiO2 i s0001dGaNsAlGaNd and f001gTiO2 i k112̄0lGaNsAlGaNd with three rotational variants of the TiO2. Transmission electron microscopy of 50 nm thick TiO2 films on GaN an...

Application of titanium dioxide (TiO2) as a photocatalyst has presented a promising avenue for the safe photocatalytic degradation of pollutants. Increasing levels of the release of pharmaceuticals in the environment and formation of the intermediates during their degradation may impose health and environmental risks and therefore require more attention. Photocatalytic degradation of acetylsali...

In this study, we use a global model to investigate the oxygen plasma cycle of PEALD of TiO2 thin films. The reactor geometry is an asymmetric capacitive coupled (CCP) radio frequency discharge and it was investigated the effect of discharge power in the range of 10-500 W, for a working pressure of 1.0 mbar, on plasma parameters: neutral and ion species densities. These are typical conditions f...

In this manuscript, for the first time, we report a combination of electrophoretic and sintering approaches for introducing gold nanoparticles into nanoporous TiO2 films to generate 'hot' electrons resulting in a strong enhancement of photocurrent. The Au-TiO2 nanocomposite material was prepared by the electrophoretic deposition of gold nanoparticles into a porous nanoparticulate titanium dioxi...