[ 1 ] - Synthesis of Nano-Sized Titania Particles by Hydrolysis of Titanium Tetrachloride
Nano-sized titanium dioxide TiO2 powder was successfully prepared from its precursor titanium (IV) chloride by a simple and new wet chemical method. TiCl4 were used as precursor in hydrogen peroxide, H2O2 and ethanol. This solution was then peptized using nitric acid and heated under reflux at 80°C. Their physico-chemical properties were then characterized by transmission electron microscopy (T...
[ 2 ] - Low Temperature Synthesis of α-Fe2O3 Nano-rods Using Simple Chemical Route
Iron oxide (Fe2O3) is widely used as a catalyst, pigment and gas sensitive material. In this article, α-Fe2O3 nano-rods were first synthesized via a simple chemical method using iron(III) nitrate 9- hydrate (Fe(NO3)3.9H2O) as precursor. XRD pattern showed that the iron oxide nanoparticles exhibited alpha-Fe2O3 (hematite) structure in nanocrystals. The single-phase α- Fe2O3 nano-rods were prepa...
[ 3 ] - خواص مغناطیسی بلوری آلیاژ نانوذرات آهن- پلاتین (L10-FePt) در گذار فاز
High magneto- crystalline anisotropy (ku=7×106j/m3) of L10-FePt nanoparticles are an excellent candidate for ultra high-density magnetic recording. The 4 nm FePt nanocrystals were prepared by superhydride reduction of FeCl2·4H2O and Pt(acac)2 precursors in the phenyl ether by reduction of the 1, 2-hexadecanediol and LiBEt3H superhydride. The crystal and magnetic structures were studied by XRD a...
[ 4 ] - بررسی خواص بلوری و اپتیکی نانوذرات TiO2آلائیده با اتم‌های سریم تهیه شده با روش شیمیایی سل ژل
آلاییدن نانوذرات دی اکسید تیتانیوم (TiO2) با فلزات واسطه میتواند خواص فیزیکی آن را تغییر دهد. در این تحقیق نانوذرات خالص TiO2 و ناخالص Ce-doped TiO2 با درصد مولی %20 با استفاده از تتراتیتانیم ایزوپروپوکساید (TTIP) به عنوان ماده پایه و نیترات سریم به عنوان ماده ناخالصی، ساخته شدند. ساختار نمونهها توسط آنالیز پراش اشعه ایکس (XRD) مورد ارزیابی قرار گرفت. اندازه نانوذرات با وجود ناخالصی Ce، کاه...
[ 5 ] - Synthesis of Nano-Sized Titania Particles by Hydrolysis of Titanium Tetrachloride
Nano-sized titanium dioxide TiO2 powder was successfully prepared from its precursor titanium (IV) chloride by a simple and new wet chemical method. TiCl4 were used as precursor in hydrogen peroxide, H2O2 and ethanol. This solution was then peptized using nitric acid and heated under reflux at 80°C. Their physico-chemical properties were then characterized by transmission electron microscopy (T...