Objective:This study investigated the cervicalmicroleakage between titanium and three porcelain systems. Material andMethods:The titanium used in this study (commercially pure, grade 2, IMNR Bucharest, Romania) was veneered with three porcelain systems specially designed for fusing on titanium: Ti22 (Noritake, Nishikamogun, Aichi, Japan), Triceram (Esprident, Ispringen, Germany) andVitatitanker...

OBJECTIVE This study evaluated the influence of porcelain (VM9, VITA Zahnfabrik, Germany) thickness on the flexural strength and crack propagation in bilayered zirconia systems (YZ, VITA Zahnfabrik, Germany). MATERIAL AND METHODS Thirty zirconia bars (20.0x4.0x1.0 mm) and six zirconia blocks (12.0x7.5x1.2 mm) were prepared and veneered with porcelain with different thickness: 1 mm, 2 mm, or 3...

The aims of this study were to determine the fracture origins and crack paths in the porcelain of clinically failed bilayer ceramic restorations and to reveal the correlation between the porcelain failures and material properties. Three clinically failed crowns of each material (bilayer zirconia crowns, galvano-ceramic crowns, and porcelain-fused-to-metal crowns) were collected and underwent fa...

The royal porcelain manufactories in eighteenth-century Continental Europe were sites of production that implemented chemistry in three different areas: manufacture of porcelain paste, preparation of pigments for ornamenting porcelain, and construction of furnace along with choice of fuel for firing porcelain. This paper provides evidence for the Royal Prussian Porcelain Manufactory in Berlin b...

In this study, two types of porous zirconia and dense zirconia were used. The flexural strength of non-layered zirconia specimens and those of the layered zirconia specimens with veneering porcelain were examined. Furthermore, the shear bond strength of veneering porcelain to zirconia was examined. The flexural strength of the non-layered specimens was 1,220 MPa for dense zirconia and 220 to 30...

D6056 prefabricated abutment includes placement D6057 custom abutment includes placement D6058 abutment supported porcelain/ceramic crown D6059 abutment supported porcelain fused to metal crown (high noble metal) D6060 abutment supported porcelain fused to metal crown (predominantly base metal) D6061 abutment supported porcelain fused to metal crown (noble metal) D6062 abutment supported cast m...

Plasma and halogen lamp units were used to photo-cure a composite resin for porcelain bonding. Mean shear bond strengths to dentin after light curing through porcelain of 1 and 2 mm thickness ranged from 20 to 27 MPa before and after thermocycling, indicating no significant effects due to porcelain thickness, curing method, or thermocycling, except for plasma curing for 3 s through porcelain of...

STATEMENT OF PROBLEM Bonded porcelain veneers are widely used esthetic restorations. Although high success and survival rates have been reported, failures occur. Fracture is the most common failure mode. Fractures range from incomplete cracks to the catastrophic. Minimally invasive or thin partial veneers have gained popularity. PURPOSE The aim of this study was to measure the influences of p...

BACKGROUND This study evaluated the feasibility of fabricating implant abutments and crowns from pre-sintered feldspathic porcelain blocks using the chair-side CAD/CAM, CEREC3D((R)) system. METHODS Thirty-two implant analogues were divided into two groups. In the control group, prefabricated machined anatomical titanium (Ti) abutments were screw-retained to the analogues. In the test group, m...

This investigation examined the marginal characteristics of the collarless metal ceramic restoration made with two commonly used direct-lift techniques: (1) a porcelain/wax paste and (2) a porcelain/liquid slurry. The metal copings touched the shoulder in half of the groups and were left 0.5 mm short in the other half to comprise the four experimental groups. Marginal seal was evaluated at faci...