Bio-Based Polyols from Seed Oils for Water-Blown Rigid Polyurethane Foam Preparation
نویسندگان
چکیده
منابع مشابه
Producing Lignin-Based Polyols through Microwave-Assisted Liquefaction for Rigid Polyurethane Foam Production
Lignin-based polyols were synthesized through microwave-assisted liquefaction under different microwave heating times (5-30 min). The liquefaction reactions were carried out using polyethylene glycol (PEG-400)/glycerol as liquefying solvents and 97 wt% sulfur acid as a catalyst at 140 °C. The polyols obtained were analyzed for their yield, composition and structural characteristics using gel pe...
متن کاملPolyols from Microwave Liquefied Bagasse and Its Application to Rigid Polyurethane Foam
Bagasse flour (BF) was liquefied using bi-component polyhydric alcohol (PA) as a solvent and phosphoric acid as a catalyst in a microwave reactor. The effect of BF to solvent ratio and reaction temperatures on the liquefaction extent and characteristics of liquefied products were evaluated. The results revealed that almost 75% of the raw bagasse was converted into liquid products within 9 min a...
متن کاملBio-Based Rigid Polyurethane Foam from Liquefied Products of Wood in the Presence of Polyhydric Alcohols
Rigid polyurethane foams were prepared from the liquefied wood polyols, which was obtained by the liquefaction of southern pine wood in the presence of polyhydric alcohols with sulfuric acid catalyst by using microwave-assistant as an energy source. The properties of liquefied biomass-based polyols and the rigid polyurethane foams were investigated. The results indicated that the foams exhibite...
متن کاملSynthesis and Characterization of Polyols from Refined Cooking Oil for Polyurethane Foam Formation Synthesis and Characterization of Polyols from Refined Cooking Oil for Polyurethane Foam Formation
Chemical Engineering, School of Engineering and Information Technology, Universiti Malaysia Sabah, UMS Road, 88400 Kota Kinabalu, Sabah, Malaysia *School of Chemical Sciences, Universiti Sains Malaysia, 11800 Penang, Malaysia **School of Dental Sciences, Health Campus, Universiti Sains Malaysia, 16150 Kubang Kerian, Kelantan, Malaysia ***Malaysian Institute Pharmaceutical & Nutraceutical, MOSTI...
متن کاملNonlinear Optical Properties of Rigid Polyurethane Foam/SiO2 Nanocomposite
Polyurethane closed cell (PUCC)/SiO2 nanocomposites have been prepared by using in situ polymerization approach. The third-order optical nonlinearities of PUCC/SiO2 nanocomposites, dissolved in DMF are characterized by Z-scan technique at the measurement wavelength of 532 nm. The nonlinear refractive (NLR) indices and nonlinear absorption (NLA) coefficients of samples were calculated from close...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Polymer Science
سال: 2016
ISSN: 1687-9422,1687-9430
DOI: 10.1155/2016/4909857