Correlation between Intergranular Corrosion and Impurities of Extra High Purity Austenitic Stainless Steels
نویسندگان
چکیده
منابع مشابه
Influence of Silicon, Carbon and Phosphorus on Intergranular Corrosion of High Purity Austenitic Stainless Steels Under Transpassive Conditions
Precipitate-free Fe-Cr-Ni f.c.c. alloys exhibit strong intergranular corrosion in acid solutions at electrochemical potentials from the transpassivity range. Segregation of impurity atoms to grain boundaries is generally considered to be responsible for this specific kind of localized damage. A study of the influence of silicon, phosphon~s and carbon on the intergranular transpassive corrosion ...
متن کاملLow-Temperature Carburization of Austenitic Stainless Steels
LOW-TEMPERATURE CARBURIZATION is a gaseous carburization process performed at atmospheric pressure, at temperatures where the kinetics of substitutional diffusion are very slow. Low-temperature carburization hardens the surface of austenitic stainless steels through the diffusion of interstitial carbon, without the formation of carbides. The surface must be activated, by modification and remova...
متن کاملDevelopment of Alumina-Forming Austenitic Stainless Steels
This paper presents the results of the continued development of creep-resistant, alumina-forming austenitic (AFA) stainless steel alloys, which exhibit a unique combination of excellent oxidation resistance via protective alumina (Al2O3) scale formation and high-temperature creep strength through the formation of stable nano-scale MC carbides and intermetallic precipitates. Efforts in fiscal ye...
متن کاملY Studies on Austenitic Stainless Steels
Abstract--In this investigation, the fracture surfaces of SS 304 and SS 316 austenitic steels were analysed using the X-ray fractography technique. In both cases, a decrease in the austenite content was observed at the fracture surface as a result of deformation induced martensite, indicating a linear relation with Km~ within the stable crack growth region. The presence of this martensite was f...
متن کاملGrain Boundary Oxidation and the Chromium- Depletion Theory of Intercrystalline Corrosion of Austenitic Stainless Steels
High temperature microscopy during oxidation of austenitic stainless steels shows that an increased rate of oxidation is found in a narrow zone along grain boundaries where chromium carbides have been precipitated. This lends support to the chromium-depletion theory of intercrystatline corrosion of these steels. Approximate solution of the appropriate diffusion problem shows good agreement with...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Power and Energy Systems
سال: 2010
ISSN: 1881-3062
DOI: 10.1299/jpes.4.105