Dephosphorization of Molten High Chromium Iron with CaO-based Flux
نویسندگان
چکیده
منابع مشابه
Tribological Behavior of Reinforced and Unreinforced High Chromium Cast Iron
In this paper, the metal matrix composites containing 22 wt % Cr, 2.5 wt % C and 2 to 16 volume percent TiC were processed by solidifying Fe-Cr-Ti-C in which precipitation of titaniumcarbide and chromium carbide occurred. The microstructure and abrasion resistance of in-situ synthesized composites were compared with the unreinforced high chromium white cast iron (HCWCI) containing 22 w. t. % C...
متن کاملThe Effect of Flux type and Oxygen Blowing on Simultaneous Removal of Phosphorus and Sulfur from Molten Iron
This research was conducted to study the effect of lime based Flux with the composition of CaO-20%CaF2-8%FeO on simultaneous removal of phosphorus and Sulfur from hot metal. The effects of Na2O and oxygen blowing were also studied. The experiments were performed using an induction furnace and hot metal produced in Isfahan Steel Company in the temperature range 1350-1450 ºC...
متن کاملReaction Behavior of Phosphorus in Coal-Based Reduction of an Oolitic Hematite Ore and Pre-Dephosphorization of Reduced Iron
Coal-based reduction followed by magnetic separation is an effective way to recover iron from high phosphorus-containing oolitic hematite ore. Given that high quantities of dephosphorization agent are needed to obtain low phosphorus reduced iron, a novel approach is proposed by the authors. Without prior phosphorus removal, the phosphorus was enriched in the reduced iron during a reduction proc...
متن کاملIron� High Magnetic Field Behavior of Impurities Chromium� In
THE PRESENCE of small amounts of iron in chromium metal results in a lowering of the Neel temperature along with other anomalous diagram[l, changes in the phase r 1 , 2]. Suscepti[I] N eel bility measurements 1 below the temperature show that the iron sites have associated with them localized magnetic moments of about 1·4f.LIJ I· per iron atom and that the iron moments remain paramagnetic do...
متن کاملWettability of Carbonaceous Materials with Molten Iron at 1550°C
In the direct iron smelting process, interfacial reactions of carbonaceous materials with molten iron are among some of the key factors that dictate the rate of carbon transfer into molten iron and establish a carbon concentrated melt to reduce iron oxide in the slag phase. Detailed wettability investigations on a range of carbonaceous materials, e.g. synthetic graphite, natural graphite, coke,...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 1992
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane1955.78.2_231