Effect of stress frequency on fatigue crack initiation.
نویسندگان
چکیده
منابع مشابه
Side Effects of Shot Peening on Fatigue Crack Initiation Life
Shot peening beneficial effects on fatigue life of mechanical components are well known. However, there are some reports in the literature that indicate inappropriate shot peening parameters tend to reduce the fatigue life. It is therefore, the purpose of this study to find a logical quantitative justification for these observations. Using finite element method, a dynamic elastic-plastic simula...
متن کاملAn Outrun Competition of Corrosion Fatigue and Stress Corrosion Cracking on Crack Initiation in a Compressor Blade
First row rotating blades of four axial-flow compressors were prematurely fractured. Previous investigations showed that the site atmosphere contains corrosive compounds which lead to an increase in possibility of pitting on the blades. It was also revealed that the crack was originated from two corrosion pits. Thus, this work is conducted to ascertain which of fatigue or stress corrosion crack...
متن کاملEffects of Microstructure on Room Temperature Fatigue Crack Initiation and Short Crack Propagation in Udimet
An assessment of the effects of microstructure on room temperature fatigue crack initiation and short crack propagation in a Ni-base superalloy is presented. The assessment was carried out on microstructural variants of U720Li, including as-received U720Li, U720Li-LG (large grain variant) and U720Li-LP (large intragranular coherent γ′ variant). Fatigue tests were carried out at room temperature...
متن کاملFatigue Crack Initiation and Multiplication of Unnotched Titanium Matrix Composites
ÐFatigue crack initiation and multiplication of the unnotched SCS-6 silicon carbide ®ber-reinforced titanium matrix composites with dierent matrix and interfacial properties have been investigated experimentally and analytically. Ti±15V±3Al, Ti±6Al±4V, and Ti±22Al±23Nb were chosen as matrix materials. The initiation and propagation of each individual matrix crack as a function of fatigue cycle...
متن کاملFatigue crack initiation life prediction of railroad wheels
A new multiaxial high-cycle fatigue initiation life prediction model for railroad wheels is proposed in this paper. A general fatigue damage analysis methodology for complex mechanical components is developed and applied to the wheel/rail rolling contact fatigue problem. A 3-D elasto-plastic finite element model is used for stress analysis. A submodeling technique is used to achieve both comput...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 1985
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.34.185