Fabrication of Micro- and Nanopillars from Pyrolytic Carbon and Tetrahedral Amorphous Carbon
نویسندگان
چکیده
منابع مشابه
MAGNETISATION AND ELECTRON SPIN RESONANCE STUDIES OF TETRAHEDRAL AMORPHOUS CARBON
The magnetisation and electron spin resonance (ESR) spectrum of two specimens of tetrahedral amorphous carbon (ta-C), deposited from a filtered cathodic arc, were measured over a wide temperature range. The magnetisation was found to consist of superparamagnetic, paramagnetic and diamagnetic contributions. The superparamagnetic contribution resembled that recently found in carbon prepared from ...
متن کاملmagnetisation and electron spin resonance studies of tetrahedral amorphous carbon
the magnetisation and electron spin resonance (esr) spectrum of two specimens of tetrahedral amorphous carbon (ta-c), deposited from a filtered cathodic arc, were measured over a wide temperature range. the magnetisation was found to consist of superparamagnetic, paramagnetic and diamagnetic contributions. the superparamagnetic contribution resembled that recently found in carbon prepared from ...
متن کاملDynamic roughening of tetrahedral amorphous carbon.
The roughness of tetrahedral amorphous carbon (ta-C) films grown at room temperature is measured as a function of film thickness by atomic force microscopy, to extract roughness and growth exponents of alpha approximately 0.39 and beta approximately 0-0.1, respectively. This extremely small growth exponent shows that some form of surface diffusion and relaxation operates at a homologous tempera...
متن کاملComparing hardness and wear data for tetrahedral amorphous carbon and hydrogenated amorphous carbon thin films
We compared nanoindentation and nanoscratch testing of 10 and 50 nm thick tetrahedral amorphous carbon (ta-C) and hydrogenated amorphous carbon (a-C:H). Raman spectroscopy shows the expected spectral features for the two carbon forms, however, luminescence from the ceramic substrate can alter the spectra. We find that hard ta-C films can blunt the diamond tip and hence use a tip area function r...
متن کاملPhotoconductivity in highly tetrahedral diamondlike amorphous carbon
A photoconductive effect is observed in tetrahedral amorphous carbon (ta-C) or amorphous diamond films with a high proportion of sp3 bonding and a structure analogous to amorphous silicon. The spectral response is shown to peak at around 750400 nm and extend into the near UV region. The maximum photoresponse coincides wit.h the optical absorption edge. The quantum efficiency of 300 nm thick fil...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Micromachines
سال: 2019
ISSN: 2072-666X
DOI: 10.3390/mi10080510