Factors affecting the nitridation behavior of Fe-base, Ni-base, and Co-base alloys in pure nitrogen
نویسندگان
چکیده
منابع مشابه
Factors affecting the nitridation behavior of Fe-base, Ni-base, and Co-base alloys in pure nitrogen
The behavior of alloys in nitrogen at high temperature is relevant to many industrial applications. Embrittlement due to internal nitride formation is the principal problem encountered in service. In this study, the nitridation resistance of a series of alloys in pure nitrogen at 1093 O C was investigated. For Fe-base, Ni-base, and Co-base alloys the amount of nitrogen absorbed and the nature a...
متن کاملTernary Ni-Fe-Co Alloys Nanowire Electrodeposition
Nanowire is a cylindrical nano-structure with nanometer dimensions. In this research, the studied nanowire was made from the magnetic triple Ni-Fe-Co alloy.
 We utilized ordered porous anodic aluminum oxide as a template for the nanowire deposition. The nanowire arrays were electrodeposited in the cylindrical pores of the oxide layer by AC potential in a simple sulfate bath. Then the relatio...
متن کاملOpen-Cellular Co-Base and Ni-Base Superalloys Fabricated by Electron Beam Melting
Reticulated mesh samples of Co-29Cr-6Mo alloy and Ni-21Cr-9Mo-4Nb alloy (625) and stochastic foam samples of Co-29Cr-6Mo alloy fabricated by electron beam melting were characterized by optical metallography, and the dynamic stiffness (Young's modulus) was measured by resonant frequency analysis. The relative stiffness (E/Es) versus relative density (ρ/ρs) plotted on a log-log basis resulted in ...
متن کاملFactors affecting the bond strength of denture base and reline acrylic resins to base metal materials
OBJECTIVE The shear bond strengths of two hard chairside reline resin materials and an auto-polymerizing denture base resin material to cast Ti and a Co-Cr alloy treated using four conditioning methods were investigated. MATERIAL AND METHODS Disk specimens (diameter 10 mm and thickness 2.5 mm) were cast from pure Ti and Co-Cr alloy. The specimens were wet-ground to a final surface finish of 6...
متن کاملTernary Ni-Fe-Co Alloys Nanowire Electrodeposition
Nanowire is a cylindrical nano-structure with nanometer dimensions. In this research, the studied nanowire was made from the magnetic triple Ni-Fe-Co alloy. We utilized ordered porous anodic aluminum oxide as a template for the nanowire deposition. The nanowire arrays were electrodeposited in the cylindrical pores of the oxide layer by AC potential in a simple sulfate bath. Then the relation ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Le Journal de Physique IV
سال: 1993
ISSN: 1155-4339
DOI: 10.1051/jp4:1993915