Fatigue crack growth under variable-amplitude loading: Part I – Model formulation in state-space setting
نویسندگان
چکیده
منابع مشابه
Strip yield modelling of fatigue crack under variable amplitude loading
The results from ‘strip yield’ approach of the FASTRAN type models of plasticity induced crack closure effects of fatigue cracks subjected to variable amplitude loadings are presented. The strip yield results are compared with authors’ finite element (FE) and experimental results. It has been observed that the strip yield model is seen to be fundamentally limited by choice of α (constraint fact...
متن کاملAnalyses of Fatigue and Fatigue-crack Growth under Constant- and Variable-amplitude Loading
Studies on the growth of small cracks have led to the observation that fatigue life of many engineering materials is primarily “crack growth” from micro-structural features, such as inclusion particles, voids, slip-bands or from manufacturing defects. This paper reviews the capabilities of a plasticity-induced crack-closure model to predict fatigue lives of metallic materials using “small-crack...
متن کاملA Dynamical Coefficient Mechanics Model for Fatigue Crack Growth under Constant Amplitude Loading
Almost all load bearing components usually experience variable amplitude loading (VAL) rather than constant amplitude loading (CAL) during their service lives. Although many models have been proposed on this subject, but life prediction under these complex situations is still under constant improvement. The present study aims at evaluating residual fatigue life under CAL due to application of t...
متن کاملApplication of a strip-yield model to predict crack growth under variable-amplitude and spectrum loading – Part 1: Compact specimens
Fatigue-crack-growth tests were conducted on compact, C(T), specimens made of D16Cz (clad) aluminum alloy under constant-amplitude loading, a single spike overload, and simulated aircraft spectrum loading. Constant-amplitude tests were conducted to generate crack-growth-rate data from threshold to near fracture over a wide range of stress ratios (R = Pmin/Pmax = 0.1–0.75) using the new compress...
متن کاملTransient Fatigue-crack Growth Behavior following Variable-amplitude Loading in a Monolithic Silicon Nitride Ceramic
ÐTransient cyclic fatigue-crack growth behavior following variable-amplitude loading sequences has been investigated in a hot-pressed, monolithic Si3N4 ceramic (NTK EC-141), for which fracture toughness (resistance-curve) and cyclic fatigue properties are well characterized. Following rapid changes in the applied stress-intensity range, DK, during both low-high and high-low block-loading sequen...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Applied Mathematical Modelling
سال: 2001
ISSN: 0307-904X
DOI: 10.1016/s0307-904x(01)00026-9