Fracture modes in brittle coatings with large interlayer modulus mismatch
نویسندگان
چکیده
منابع مشابه
Fracture modes in brittle coatings with large interlayer modulus mismatch
Fracture modes in a model glass–polymer coating–substrate system indented with hard spheres are investigated. The large modulus mismatch between the glass and polymer results in distinctive transverse fracture modes within the brittle coating: exaggerated circumferential (C) ring cracks that initiate at the upper coating surface well outside the contact (as opposed to the near-contact Hertzian ...
متن کاملHydraulically pumped cone fracture in bilayers with brittle coatings
An earlier finite element modeling analysis of inner cone cracks in monolithic brittle solids subject to cyclic indentation in liquids is extended to include the case of a brittle layer bonded to a compliant substrate, using a model glass/polycarbonate bilayer system as an illustrative case study. Provision is made for incorporation of plate flexure stresses, along with hydraulic pumping stress...
متن کاملCracking of brittle coatings adhesively bonded to substrates of unlike modulus
The role of elastic mismatch in determining critical conditions for indentation fracture in brittle coatings on substrates of unlike modulus was investigated. A model transparent trilayer system, consisting of a glass coating layer bonded to a thick substrate of different glass or polymer by a thin layer of epoxy adhesive, facilitated in situ observations of crack initiation and propagation. A ...
متن کاملFracture mode transitions in brittle coatings on compliant substrates as a function of thickness
The fundamentally changing nature of fracture in brittle coatings on compliant substrates with diminishing coating thickness is examined. Attention is focused on cracking induced by concentrated loading with a spherical indenter at the top surface. It is shown that the fracture mode undergoes transitions, from top-surface ring cracking around the contact (“thick-coating” region) to bottom-surfa...
متن کاملBrittle Bone Fracture Risk with Transverse Isotropy
Osteogenesis imperfecta (OI) is a heritable bone fragility disorder characterized by skeletal deformity and “brittle” bones. This fragility is believed to stem from a combination of bone mass deficiency and compromised bone material properties [1-3]. Poor bone quality poses major orthopaedic and rehabilitation challenges. Risk of fracture is a major consideration when prescribing activity restr...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Materials Research
سال: 1999
ISSN: 0884-2914,2044-5326
DOI: 10.1557/jmr.1999.0514