Improvement of solidification cracking susceptibility of electron beam weld metal of fully austenitic Type 316 stainless steel.

Effect of grain size on solidification cracking susceptibility of type 347 stainless steel during laser welding

An evaluation of weld metal nitrogen retention and properties in 316LN austenitic stainless steel

A series of tests were conducted using varying levels of nitrogen and helium in a conventional argon shielding gas when welding 316LN austenitic stainless steel. The outcome was that a 15 per cent nitrogen addition to the argon shielding gas had the most significant effect on increasing the weld metal nitrogen. Subsequent additions of helium to the argon 15 per cent nitrogen shielding gas had v...

The adhesion of hot-filament CVD diamond films on AISI type 316 austenitic stainless steel

Steel ball indentation and scratch adhesion testing of hot filament chemical vapour deposited diamond films onto AISI type 316 austenitic stainless steel substrates using two different interlayer systems, namely chromium nitride and borided steel, have been investigated. In order to compare the adhesion of these films with that of a well-known and strongly adherent system, detailed adhesion tes...

Crystallography of Widmanstätten austenite in duplex stainless steel weld metal

Two kinds of austenite grow from d-ferrite during the cooling of the duplex stainless steel weld deposits studied here, Widmanstätten plates and allotriomorphs which precipitate at d–d grain boundaries. It is found using microtexture measurements that the preferred crystallographic orientation of the Widmanstätten austenite can be estimated using established theory if it is assumed that there i...

Fatigue behavior of Austenitic Type 316L Stainless Steel

The aim of this work is to determine the fatigue life of 316L stainless steel. The mechanisms of fatigue of 316L stainless steels were investigated and discussed. The fatigue tests were carried out at constant-amplitude cyclic loading with load ratio R=0.1. Scanning Electron Microscope (SEM) is then used to examine the fracture surface. The results show that the fatigue limit of 316L stainless ...