Kinetics of Tin Dissolution in Sodium Hydroxide Solutions
نویسندگان
چکیده
منابع مشابه
Leaching Kinetics of Stibnite in Sodium Hydroxide
Spherical pellets of antimony sulphide were dissolved in 1 molar sodium hydroxide solutions at different temperatures. It was found that the shrinking core with ash layer model could satisfactorily explain the dissolution process. Using this model it was found that initially the rate controlling step is a chemical reaction with activation energy of 10.2 kJ/mol. As the ash layer builds up, diffu...
متن کاملThe Kinetics of Saponification of Iodoacetic Acid by Sodium Hydroxide and by Certain Alkaline Buffer Solutions
1. The rate of the saponification of iodoacetic acid in sodium hydroxide and alkaline buffer solutions yielding glycollic acid was measured by means of Heyrovský's polarographic method. 2. From the bimolecular velocity constants, increasing with the ionic strength of the solution, the Brönsted factor, F, which characterizes the primary salt effect, was calculated. 3. In the borate buffer soluti...
متن کاملLeaching kinetics of gibbsitic bauxite with sodium hydroxide
In this paper the results of a leaching kinetics study of bauxite ore with sodium hydroxide are presented. The effect of ore particle size, sodium hydroxide concentration and reaction temperature on the Al2O3 extraction rate was determined. The results obtained showed that 99% of Al2O3 was leached out using -200+270 mesh ore particle size at a reaction temperature of 105 °C for 60 min reaction ...
متن کاملEffects of calcium hydroxide and sodium hypochlorite on the dissolution of necrotic porcine muscle tissue.
The dissolving effect of the endodontic medicaments calcium hydroxide (Ca(OH)2) and sodium hypochlorite (NaOCl) on necrotic tissue was studied. Pieces of necrotic porcine muscular tissue were placed in either a 0.5% NaOCI solution (Dakin's solution), Ca(OH)2 mixed with water, or a NaOCI solution following pretreatment in Ca(OH)2 for various time intervals. The tissue pieces placed in 0.5% NaOCl...
متن کاملStability of layered Ni hydroxide surface precipitates—A dissolution kinetics study
In recent years, studies have shown that sorption of metals onto natural materials results in the formation of new mineral-like precipitate phases. However, the stability of the precipitates and the potential long-term release of the metal back into the soil solution are poorly understood. Therefore, we investigated the influence of residence time and dissolution agent on the release of nickel ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1996
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.60.9_826