Leaching Behavior of Pressureless-Sintered Si3N4 Containing MgO under Hydrothermal Conditions
نویسندگان
چکیده
منابع مشابه
Microstructure and mechanical properties of pressureless sintered alumina-silver composites
The silver toughened alumina ceramics, which were fabricated via a conventional ceramic processing route using commercially available alumina and silver oxide powders as the starting materials, exhibit a higher fracture toughness (6 to 9 MPamo.5) than the monolithic alumina ceramic ( 2.5 to 3.0 MPamo.5). The weak interfacial bonding between the silver inclusions and the alumina matrix is charac...
متن کاملSpeciation of Molybdates under Hydrothermal Conditions
In situ Raman spectroscopy was applied to investigate the speciation of molybdates under hydrothermal conditions in 0.2 M aqueous solution in the temperature range between 20°C and 200°C and at pH values between 7 and 1. The nature and abundance of molecular and supra-molecular species differs significantly compared to the distribution of species under ambient conditions at the same pH. Whereas...
متن کاملContinuous-flow detoxification treatment of boron-containing wastewater under hydrothermal conditions
To develop a practical method of treating boron-containing wastewater, we custom designed two laboratory-scale continuousflow-type hydrothermal mineralization apparatuses. We carried out a hydrothermal treatment using a continuous-flow apparatus, using Ca(OH)2, CaCl2, and both Ca(OH)2 and CaCl2 as mineralizers, under various pH conditions. Our results show that using CaCl2 under optimal pH cond...
متن کاملThe Comparison of MgO and TiO2 Additives Role on Sintering Behavior and Microstructures of Reaction-Sintered Alumina-Zirconia-Mullite Composite
Alumina-Mullite-Zirconia ceramic composites were prepared by reaction sintering of alumina, zircon mixture and the sintering aids of magnesia and titania at temperatures of 1400 and 1600 C for 2 hours. The development of different phases and microstructures of the composites were analysed to assess the relative influence of the additives on the formation of alumina-zirconia-mullite compos...
متن کاملLeaching of metals from cement under simulated environmental conditions.
Leaching of metals from cement under various environmental conditions was measured to evaluate their environmental safety. A cement product containing clinker, which was produced from cement kiln co-processing of hazardous wastes, was solidified and leaching of metals was characterized using the 8-period test. Concentrations and speciation of metals in cements were determined. Effects of ambien...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Association, Japan
سال: 1987
ISSN: 1884-2127,0009-0255
DOI: 10.2109/jcersj1950.95.1103_730