Low-Temperature Superplasticity in Aluminum Alloys Processed by Equal-Channel Angular Pressing
نویسندگان
چکیده
منابع مشابه
Achieving superplasticity in a Bi-Sn alloy processed by equal- channel angular pressing
Equal-channel angular pressing (ECAP) was utilized to process a Bi‒42Sn eutectic alloy at room temperature using processing route A for 1, 2, 4, and 8 passes. Tensile testing was performed at room temperature under initial strain rates in the range of 1.0 × 10 -5 to 1.0 × 10 -2 s -1 . The results demonstrate that processing by ECAP improves the ductility in this material and the elongations to ...
متن کاملMicrostructure Evolution in High Purity Aluminum Single Crystal Processed by Equal Channel Angular Pressing (ECAP)
Aluminum single crystal with 99.999% purity was deformed at room temperature by equal channel angular pressing (ECAP) up to 16 passes. Grain size and misorientation of processed samples were quantitatively characterized by TEM and EBSD. The results show that the refinement efficiency of high purity aluminum single crystal was poor in the initial stage. Extrusion by fewer ECAP passes (n ≤ 8) res...
متن کاملSize effect in equal channel angular pressing (ECAP) process
The influence of the sample size (diameter while keeping the length constant) in equal channel angular pressing (ECAP) of pure aluminum is examined using finite element method (FEM) and experiment. Different sized aluminum rods were processed via ECAP and the effect of sample size on the strain homogeneity, process load, and the ratio of the friction to the total force were evaluated. The resul...
متن کاملRe-strengthening in AA6063 Alloy During Equal Channel Angular Pressing
Equal channel angular pressing (ECAP) is carried out using two different configurations for the exit channel of the ECAP die, i.e., relieved and choked, with angles of 0.2 °. It is found that using a die with relieved exit channel, the sample was extruded for 6 passes with no surface cracks and an average cell size of 727 nm and a fraction of high angle grain boundaries of 54 % were achieved. M...
متن کاملHigh Temperature Deformation of Twin-Roll Cast Al-Mn-Based Alloys after Equal Channel Angular Pressing
Twin roll cast Al-Mn- and Al-Mn-Zr-based alloys were subjected to four passes of equal channel angular pressing. The resulting grain size of 400 nm contributes to a significant strengthening at room temperature. This microstructure is not fully stable at elevated temperatures and recrystallization and vast grain growth occur at temperatures between 350 and 450 °C. The onset of these microstruct...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2002
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.43.2364