Mechanical and Thermal Characterisation of Millscale Modified Al-Cu Alloy for Artificial Intelligence Systems
نویسندگان
چکیده
منابع مشابه
Formation, Thermal Stability and Mechanical Properties of Cu-Zr and Cu-Hf Binary Glassy Alloy Rods
Glassy alloy rods with diameters up to 1.5mm exhibiting a large supercooled liquid region before crystallization and high mechanical strength were formed in Cu-Zr and Cu-Hf binary alloy systems by the copper mold casting method. The large supercooled liquid region exceeding 40K was obtained in the composition range of 30 to 70 at%Zr and 35 to 60 at%Hf. The largest value of the supercooled liqui...
متن کاملStudy on Microstructure and Mechanical Properties of Hypereutectic Al–18Si Alloy Modified with Al–3B
An hypereutectic Al-18Si alloy was modified via an Al-3B master alloy. The effect of the added Al-3B and the modification temperature on the microstructure, tensile fracture morphologies, and mechanical properties of the alloy were investigated using an optical microscope, Image-Pro Plus 6.0, a scanning electron microscope, and a universal testing machine. The results show that the size of the ...
متن کاملThermal Conductivity of Cu and Al-Water Nanofluids
Nanofluids are suspensions of nanoparticles in the base fluids, a new challenge for thermal sciences provided by nanotechnology. In this paper, the tested fluids are prepared by dispersing the Al and Cu into water at three different concentrations such as 500, 1000 and 2000 ppm. Thermal conductivities of these fluids are measured experimentally by thermal property analyzer i.e. KD2 Pro by using...
متن کاملMicrostructures and thermal stability of metastable - phase precipitates formed in an Al – Cu alloy at 463
The precipitation behavior in an Al– Cu alloy isothermally annealed at 463 K was studied using Vickers microhardness tests, differential scanning calorimetry (DSC) and transmission electron microscopy (TEM). An additional endothermic peak found in the DSC measurements may be attributed to the h00-phase, independent of the dissolution of the G. P. (II) and the h00-phase at the aging temperatures...
متن کاملMicrostructural evolution , strengthening and thermal stability of an ultrafine - grained Al - Cu - Mg alloy
To gain insight into the origin of the ultra-high strength of ultrafine-grained (UFG) alloys, the solute clustering, precipitation phenomena, and microstructural evolutions were studied in an UFG Al-4.63Cu-1.51Mg (wt.%) alloy (AA2024) processed by high-pressure torsion (HPT). The thermal analysis was performed using differential scanning calorimetry. The microstructures, internal microstrains a...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Institute of Engineering
سال: 2021
ISSN: 1810-3383
DOI: 10.3126/jie.v16i1.36651