Microstructure Analysis of Tungsten Carbide Hardfacing on Carbon Steel Blade
نویسندگان
چکیده
منابع مشابه
Check Tic-coated Tungsten Carbide Tool Wear in Machining Steel
In industrial production systems, including the most important factors in the economic field machining operations, reduce tool wear due to abrasive nature of the phenomenon on many factors, including temperature Lathe tool, influences, machining conditions (cutting speed, speed losses, forcing to rebuild parts of the manufacturing tolerances disassemble tool wear is caused by the phenomenon, as...
متن کاملCarbide formation in tungsten-containing amorphous carbon films by annealing
Tungsten-containing amorphous carbon films were produced by dual magnetron sputter deposition. The formation of carbide phases after heat treatment in inert gas at temperatures up to 2800 K was investigated by X-ray diffraction for tungsten concentrations below 25 at%. After deposition, each film consists of an amorphous carbon matrix with atomically dispersed W inclusions. Annealing up to 2800...
متن کاملCarbon-hydrogen bond activation over tungsten carbide catalysts
Tungsten carbides with surface areas ranging from 4 to 39 m2/g were prepared by the temperatureprogrammed carburization of tungsten oxide and nitride powders with pure C H 4 o r a 48.9% CH4 in H 2 mixture. Oxygen uptakes on the carbides were low most likely because of the presence of graphitic carbon at the surface. Nevertheless, the carbides were active and selective for the dehydrogenation of...
متن کاملCobalt with tungsten carbide
in the testicular damage caused by indium arsenide and indium phosphide in hamsters during two years after intratracheal instillations. (CIGS) nanocrystal " inks " for printable photovoltaics. Selective sequential dissolution for the determination of inorganic indium compounds in the particulate matter of emissions and workplace air. Current evaluation Conclusion from the previous Monograph (IA...
متن کاملCladding of stellite composite on carbon steel by gas tungsten arc welding (GTAW)
This paper deals with the investigation of the microstructure and hardness of steel samples cladded with satellite 6-WC composites by using gas tungsten arc welding (GTAW) process. For this purpose, steel samples were coated with unreinforced and reinforced stellite (by 20, 30 and 40 wt.% WC). The cladded samples were evaluated by metallographic studies, microhardness measurement and X-ray diff...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: IOP Conference Series: Materials Science and Engineering
سال: 2017
ISSN: 1757-8981,1757-899X
DOI: 10.1088/1757-899x/203/1/012014