Optimum sintering conditions for optical properties of translucent aluminum nitride ceramics
نویسندگان
چکیده
منابع مشابه
Preparation of translucent YAG:Ce ceramics by reaction sintering
The paper presents preparation of YAG precursor powders mixture with ability for the reaction sintering at lower temperature. The powder mixture was mechanochemically processed and characterized for the specific surface area and crystallinity (XRD). Sintering experiments were performed on the batched powders, mechanochemically processed powders and as-synthesised YAG powders. XRD measurements a...
متن کاملcontrol of the optical properties of nanoparticles by laser fields
در این پایان نامه، درهمتنیدگی بین یک سیستم نقطه کوانتومی دوگانه(مولکول نقطه کوانتومی) و میدان مورد مطالعه قرار گرفته است. از آنتروپی ون نیومن به عنوان ابزاری برای بررسی درهمتنیدگی بین اتم و میدان استفاده شده و تاثیر پارامترهای مختلف، نظیر تونل زنی(که توسط تغییر ولتاژ ایجاد می شود)، شدت میدان و نسبت دو گسیل خودبخودی بر رفتار درجه درهمتنیدگی سیستم بررسی شده اشت.با تغییر هر یک از این پارامترها، در...
15 صفحه اولSintering of Ceramics
Sintering with low frequency rf power (-50 M H z ) is a new technique with unique capabilities that has been used to sinter a variety of ceramic materials, including zirconia-toughened alumina, alumina, silicon carbide, and boron carbide. Processing with low frequencies offers many advantages compared to processing with conventional microwave frequencies (915 MHz and 2.45 GHz). Because of the l...
متن کاملProcessing, Mechanical and Optical Properties of Additive-Free ZrC Ceramics Prepared by Spark Plasma Sintering
In the present study, nearly fully dense monolithic ZrC samples are produced and broadly characterized from microstructural, mechanical and optical points of view. Specifically, 98% dense products are obtained by Spark Plasma Sintering (SPS) after 20 min dwell time at 1850 °C starting from powders preliminarily prepared by Self-propagating High-temperature Synthesis (SHS) followed by 20 min bal...
متن کاملSintering Behavior and Properties of Iron-Rich Glass-Ceramics
Iron-rich glass-ceramics were obtained by the sintering of two glass powders, labeled G1 and G2, at heating rates of 5° and 20°C/min followed by an isothermal step in the 850°–1050°C temperature interval. The sintering process was evaluated by the linear shrinkage; the closed porosity was estimated by density measurements; the structure and the morphology of the glass ceramics were observed by ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Science Bulletin
سال: 2009
ISSN: 2095-9273,2095-9281
DOI: 10.1007/s11434-009-0115-5