Phase Transitions and Low-temperature Structure of Lithium Manganese Oxide Spinel
نویسندگان
چکیده
منابع مشابه
Phase Transitions and Low-temperature Structure of Lithium Manganese Oxide Spinel
Low-temperature structures of the lithium manganese spinels were determined using TOF neutron Rietveld analysis. The spinels LiMn2O4 with different values, (0.016, 0.040, and 0.132) showed the cubic-orthorhombic phase transitions, and the lattice distortion decreased with decreasing . Although no anomaly corresponding to the cubic-orthorhombic phase transition was observed in the DSC curve for ...
متن کاملSuppressing Manganese Dissolution from Lithium Manganese Oxide Spinel Cathodes with SingleLayer Graphene
Dr. L. Jaber-Ansari, Dr. K. P. Puntambekar, S. Kim, M. Aykol, Dr. J. Wu, B. D. Myers, R. Kumar, Prof. V. P. Dravid, Prof. C. Wolverton, Prof. M. C. Hersam Department of Materials Science and Engineering Northwestern University Evanston , IL 60208 , USA E-mail: [email protected] Dr. L. Luo, Dr. J. Wu, B. D. Myers, Prof. V. P. Dravid NU ANCE Center Northwestern University Evanston , IL 60...
متن کاملLOW TEMPERATURE SYNTHESIS OF NANOCRYSTALLINE MgAl2O4 SPINEL VIA SUCROSE PROCESS
Abstract: Nanocrystalline MgAl2O4 spinel powder was synthesized using metal nitrates and a polymer matrix-based composed of sucrose and polyvinyl alcohol (PVA). The precursor and the calcined powders were characterized by simultaneous thermal analysis (STA), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), and scanning electron microscopy (SEM). According to XRD res...
متن کاملSynthesis and characterization of manganese oxide and cobalt oxide nano-structure
The preparation of nanostructure type manganese oxide and cobalt oxide materials with the smallest particle size is reported here. The nanorod manganese oxide and cobalt oxide nanotube were prepared via a sol-gel reaction in reverse micelles from KMnO4 and CoCl2 with respectively source at room-temperature. The structure and surface morphology of the obtained manganese oxide were studied by mea...
متن کاملDependence of structure and temperature for lithium-rich layered-spinel microspheres cathode material of lithium ion batteries
Homogeneous lithium-rich layered-spinel 0.5Li2MnO3·0.5LiMn1/3Ni1/3Co1/3O2 microspheres (~1 μm) are successfully prepared by a solvothermal method and subsequent high-temperature calcinations process. The effects of temperature on the structure and performance of the as-prepared cathode material are systemically studied by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2004
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.45.2048