Preparation and Characterization of Urea Formaldehyde @ Epoxy Resin Microcapsule on Waterborne Wood Coatings
نویسندگان
چکیده
منابع مشابه
Microstructural and Micromechanical Characterization of Modified Urea-Formaldehyde Resin Penetration into Wood
Characterization of the adhesive penetration behavior in wood is highly desired for optimizing the manufacturing processes and product properties. In this study, modified urea-formaldehyde (UF) adhesive was used to prepare glued laminated timber (Cryptomeria fortunei Hooibrenk). The depth of gross penetration was measured by fluorescence microscopy (FM), which showed the UF passed through 1.5 t...
متن کاملPerformance Characterization of Coatings on Treated-wood
Coating performance is greatly influenced by the properties of the wood substrate. This study was focused on evaluating the performance of coatings on both preservative- and thermally-treated wood. A number of commercially formulated semi-transparent stains Alkyd, Alkyd-Acrylic and PU were applied on four different types of preservative treated and heat-treated wood and their performances were ...
متن کاملPreparation and Characterization of Novolak Phenol Formaldehyde Resin from Liquefied Brown-Rotted Wood
The brown-rotted wood was liquefied in phenol with phosphoric acid as catalyst and the resulting liquefied products were condensed with formaldehyde to yield novolak liquefied wood-based phenol formaldehyde resin (LWPF). The results showed that brown-rotted wood could be more easily liquefied than sound wood in phenol. The residue content of liquefied wood decreased continually with the progres...
متن کاملSynthesis, Characterization and Composites from Resorcinol-urea-formaldehyde-casein Resin
condensation reaction of urea, casein and formaldehyde in the presence of varying proportion of resorcinol under alkaline condition. All the prepared resins were characterized by free-formaldehyde content, free-phenol content, viscosity measurements and infrared spectroscopy (IR). The resin samples were cured isothermally at 120oC using two different curing agents, p-toluene sulphonic acid (PTS...
متن کاملOptimization of a Waterborne Epoxy Coatings Formulation via Experimental Design
Waterborne Epoxy based coatings were prepared by using a water-borne epoxy resin and a suitable hardener. The formulation and optimization procedure were carried out on the bases of experimental designs by the mixture design technique in which the important paint properties are modeled by using special cubic model. The corrosion behavior of these coatings was investigated using electrochemical ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Coatings
سال: 2019
ISSN: 2079-6412
DOI: 10.3390/coatings9080475