Preparation, Characterization and Sensitive Gas Sensing of Conductive Core-sheath TiO2-PEDOT Nanocables
Conductive core-sheath TiO(2)-PEDOT nanocables were prepared using electrospun TiO(2) nanofibers as template, followed by vapor phase polymerization of EDOT. Various techniques were employed to characterize the sample. The results reveal that the TiO(2) core has an average diameter of ∼78 nm while the PEDOT sheath has a uniform thickness of ∼6 nm. The as-prepared TiO(2)-PEDOT nanocables display...
متن کاملElectrospun TiO2 nanofibers for gas sensing applications
Nanostructured TiO2 has attracted much attention for a variety of applications including photocatalysts, electrodes for water photolysis, dye-sensitized solar cells, and gas sensors. In this work we report on TiO2 fiber mats for use in gas sensors demonstrating exceptionally high sensitivity to NO2, a toxic gas responsible for acid rain and other air pollution effects, and high sensitivity to H...
متن کاملNanocrystalline TiO2/SnO2 heterostructures for gas sensing
The aim of this research is to study the role of nanocrystalline TiO2/SnO2 n-n heterojunctions for hydrogen sensing. Nanopowders of pure SnO2, 90 mol % SnO2/10 mol % TiO2, 10 mol % SnO2/90 mol % TiO2 and pure TiO2 have been obtained using flame spray synthesis (FSS). The samples have been characterized by BET, XRD, SEM, HR-TEM, Mössbauer effect and impedance spectroscopy. Gas-sensing experiment...
متن کاملA visible light driven doped TiO2 nanophotocatalyst: Preparation and characterization
A useful nanophotocatalyst (La,S-TiO2) was prepared by a sol-gel method and characterized by UV–vis diffuse reflectance spectroscopy (DRS), X-ray diffraction (XRD), photoluminescence emission spectroscopy (PL) and scanning electron microscopy (FESEM). The results showed that the La,S-TiO2, which calcined at 550 °C, contained only anatase phaseand its crystal size was 23 nm...
متن کاملA visible light driven doped TiO2 nanophotocatalyst: Preparation and characterization
A useful nanophotocatalyst (La,S-TiO2) was prepared by a sol-gel method and characterized by UV–vis diffuse reflectance spectroscopy (DRS), X-ray diffraction (XRD), photoluminescence emission spectroscopy (PL) and scanning electron microscopy (FESEM). The results showed that the La,S-TiO2, which calcined at 550 °C, contained only anatase phaseand its crystal size was 23 nm...