Probing the densification mechanisms during flash sintering of ZnO
نویسندگان
چکیده
منابع مشابه
Probing the densification mechanisms during flash sintering of ZnO
Using ZnO as a model system, the densification mechanisms of flash sintering are investigated. Controlled experiments via limiting the maximum current or the effective ramp rate suggest that both the maximum specimen temperature and the high heating rate (on the order of 200 C/s) are essential for the rapid densification during the flash sintering. Moreover, benchmarking rapid thermal annealing...
متن کاملTwo-step flash sintering of ZnO: Fast densification with suppressed grain growth
Article history: Received 19 June 2017 Received in revised form 14 July 2017 Accepted 14 July 2017 Available online xxxx Two-step flash sintering (TSFS) was proposed as a new ceramic fabrication method to achieve fast densification with suppressed grain growth. Using ZnO as an examplar, ~96.5% of theoretical density was achieved using TSFS with a grain size of ~370 nm, representing a N3 times r...
متن کاملLiquid Film Capillary Mechanism for Densification of Ceramic Powders during Flash Sintering
Recently, local melting of the particle surfaces confirmed the formation of spark and plasma during spark plasma sintering, which explains the rapid densification mechanism via liquid. A model for rapid densification of flash sintered ceramics by liquid film capillary was presented, where liquid film forms by local melting at the particle contacts, due to Joule heating followed by thermal runaw...
متن کاملSintering Effects on the Densification of Nanocrystalline Hydroxyapatite
The effects of sintering profiles on the densification behaviour of synthesized nanocrystalline hydroxyapatite (HA) powder were investigated in terms of phase stability and mechanical properties. A wet chemical precipitation method was successfully employed to synthesize a high purity and single phase HA powder. Green HA compacts were prepared and subjected to sintering in air atmosphere over a...
متن کاملThermal runaway, flash sintering and asymmetrical microstructural development of ZnO and ZnO–Bi2O3 under direct currents
DC flash sintering of both pure and 0.5 mol.% Bi2O3-doped ZnO at a relatively high activating field of 300 V/cm has been investigated. It is demonstrated that even high-purity ZnO single crystals can “flash” at 870 C. In comparison, flash sintering occurs at a substantially lower onset temperature of 550 C in ZnO powder specimens, indicating the important roles of surfaces and/or grain boundari...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Materialia
سال: 2017
ISSN: 1359-6454
DOI: 10.1016/j.actamat.2016.12.015