Solar-Blind AlGaN-Based p-i-n Photodiodes With Low Dark Current and High Detectivity
نویسندگان
چکیده
منابع مشابه
High bandwidth-efficiency solar-blind AlGaN Schottky photodiodes with low dark current
Al0.38Ga0.62N/GaN heterojunction solar-blind Schottky photodetectors with low dark current, high responsivity, and fast pulse response were demonstrated. A five-step microwave compatible fabrication process was utilized to fabricate the devices. The solarblind detectors displayed extremely low dark current values: 30lm diameter devices exhibited leakage current below 3fA under reverse bias up t...
متن کاملHigh-Performance Solar-Blind AlGaN Schottky Photodiodes
High-performance solar-blind AlGaN-based Schottky photodiodes have been demonstrated. The detectors were fabricated on MOCVD-grown AlGaN/GaN hetero-structures using a microwavecompatible fabrication process. Current-voltage, spectral responsivity, noise, and high-speed characteristics of the detectors were measured and analyzed. Dark currents lower than 1 pA at bias voltages as high as 30 V wer...
متن کاملHigh-speed characterization of solar- blind AlxGa1−xN p–i–n photodiodes
We report on the temporal pulse response measurements of solar-blind AlxGa1−xN-based heterojunction p–i–n photodiodes. High-speed characterization of the fabricated photodiodes was carried out at 267 nm. The bandwidth performance was enhanced by an order of magnitude with the removal of the absorbing p+ GaN cap layer. 30 μm diameter devices exhibited pulse responses with ∼70 ps pulse width and ...
متن کاملHigh-Speed Visible-Blind Resonant Cavity Enhanced AlGaN Schottky Photodiodes
We have designed, fabricated and tested resonant cavity enhanced visible-blind AlGaN-based Schottky photodiodes. The bottom mirror of the resonant cavity was formed with a 20 pair AlN/ Al0.2Ga0.8N Bragg mirror. The devices were fabricated using a microwave compatible fabrication process. Au and indium-tin-oxide (ITO) thin films were used for Schottky contact formation. ITO and Au-Schottky devic...
متن کاملHigh Detectivity All-Printed Organic Photodiodes.
All-printed organic photodiode arrays on plastic are reported with average specific detectivities of 3.45 × 10(13) cm Hz(0.5) W(-1) at a bias of -5 V. The blade-coated polyethylenimine cathode interlayer and active layer, and screen-printed anode enable precise device performance tunability and excellent homogeneity at centimetric scales. These devices' high operational reverse bias, good linea...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: IEEE Photonics Technology Letters
سال: 2004
ISSN: 1041-1135
DOI: 10.1109/lpt.2004.829526