Solar-blind AlGaN-based Schottky photodiodes with low noise and high detectivity
نویسندگان
چکیده
منابع مشابه
High-Performance Solar-Blind AlGaN Schottky Photodiodes
High-performance solar-blind AlGaN-based Schottky photodiodes have been demonstrated. The detectors were fabricated on MOCVD-grown AlGaN/GaN hetero-structures using a microwavecompatible fabrication process. Current-voltage, spectral responsivity, noise, and high-speed characteristics of the detectors were measured and analyzed. Dark currents lower than 1 pA at bias voltages as high as 30 V wer...
متن کاملHigh bandwidth-efficiency solar-blind AlGaN Schottky photodiodes with low dark current
Al0.38Ga0.62N/GaN heterojunction solar-blind Schottky photodetectors with low dark current, high responsivity, and fast pulse response were demonstrated. A five-step microwave compatible fabrication process was utilized to fabricate the devices. The solarblind detectors displayed extremely low dark current values: 30lm diameter devices exhibited leakage current below 3fA under reverse bias up t...
متن کاملHigh-Speed Visible-Blind Resonant Cavity Enhanced AlGaN Schottky Photodiodes
We have designed, fabricated and tested resonant cavity enhanced visible-blind AlGaN-based Schottky photodiodes. The bottom mirror of the resonant cavity was formed with a 20 pair AlN/ Al0.2Ga0.8N Bragg mirror. The devices were fabricated using a microwave compatible fabrication process. Au and indium-tin-oxide (ITO) thin films were used for Schottky contact formation. ITO and Au-Schottky devic...
متن کاملLow Noise, High Detectivity Photodetectors based on Organic Materials
Organic photodetectors (OPDs) are potentially useful in many applications because of their light weight, flexibility and good form factors. Despite the high detectivities that have been frequently reported for OPDs recently, the application of these OPDs for weak light detection has been rarely demonstrated. In this thesis, low noise, high gain photodetectors based on organic and ZnO nanopartic...
متن کاملHigh Detectivity All-Printed Organic Photodiodes.
All-printed organic photodiode arrays on plastic are reported with average specific detectivities of 3.45 × 10(13) cm Hz(0.5) W(-1) at a bias of -5 V. The blade-coated polyethylenimine cathode interlayer and active layer, and screen-printed anode enable precise device performance tunability and excellent homogeneity at centimetric scales. These devices' high operational reverse bias, good linea...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Applied Physics Letters
سال: 2002
ISSN: 0003-6951,1077-3118
DOI: 10.1063/1.1516856