Strengthening Effect Analysis of Laser Shock Processing on Aluminum Alloy Welded Joint Process
نویسندگان
چکیده
منابع مشابه
The effect of surface roughness on 1050 aluminum alloy weld profile welded by pulsed Nd:YAG laser
Surface roughness in the welding processes is one of the important parameters in the laser welded metal connections which affects laser beam absorption directly. When the laser beam is irradiated to the surface of the base metal, the surface roughness plays an important role in the amount of beam absorption and the amount of melting achieved and directly affects the penetration depth. The main ...
متن کاملThe effect of surface roughness on 1050 aluminum alloy weld profile welded by pulsed Nd:YAG laser
Surface roughness in the welding processes is one of the important parameters in the laser welded metal connections which affects laser beam absorption directly. When the laser beam is irradiated to the surface of the base metal, the surface roughness plays an important role in the amount of beam absorption and the amount of melting achieved and directly affects the penetration depth. The main ...
متن کاملEvaluation Model of Aluminum Alloy Welded Joint Low-Cycle Fatigue Data Based on Information Entropy
An evaluation model of aluminum alloy welded joint low-cycle fatigue data based on information entropy is proposed. Through calculating and analyzing the information entropy of decision attributes, quantitative contribution of stress concentration, plate thickness, and loading mode to the fatigue destruction are researched. Results reveal that the total information entropy of the fatigue data b...
متن کاملThe strengthening mechanism of a nickel-based alloy after laser shock processing at high temperatures
We investigated the strengthening mechanism of laser shock processing (LSP) at high temperatures in the K417 nickel-based alloy. Using a laser-induced shock wave, residual compressive stresses and nanocrystals with a length of 30-200 nm and a thickness of 1 μm are produced on the surface of the nickel-based alloy K417. When the K417 alloy is subjected to heat treatment at 900 °C after LSP, most...
متن کاملJoint properties of cast Fe-Pt magnetic alloy laser-welded to Co-Cr alloy.
This study investigated the joint properties of Fe-Pt alloy laser-welded to Co-Cr alloy. Cast plates (0.5 x 3.0 x 10 mm) were prepared with Fe-Pt and Co-Cr alloys. Fe-Pt plates were butted against Co-Cr plates and laser-welded using Nd:YAG laser. Control and homogeneously welded specimens were also prepared. Laser welding was performed with and without argon shielding. Tensile testing was condu...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Procedia Engineering
سال: 2015
ISSN: 1877-7058
DOI: 10.1016/j.proeng.2015.12.258