Strengthening of Platinum-5 wt.% Copper by Heat Treatment
نویسندگان
چکیده
منابع مشابه
THE EFFECT OF HEAT TREATMENT ON ABRASIVE WEAR RESISTANCE OF Fe-34Cr-4.5C%WT HARDFACING ALLOY
Abstract: Hardfacing is one of the most useful and economical ways to increase the service life of components subjected to abrasive wear. Iron based hardfacing alloys have long been considered as candidate coatings for wear-resistant applications in industry. In the present work two layer of Fe-34Cr-4.5C%wt hardfacing alloy was deposited on ASTM A36 carbon steel plates by SMAW method. The m...
متن کاملTEM Characterization and Properties of Cu-1 wt.% TiB2 Nanocomposite Prepared by Rapid Solidification and Subsequent Heat Treatment
Copper matrix composite reinforced by 1wt.% TiB2 particles was prepared using in situ reaction of Cu-1.4wt.% Ti and Cu-0.7wt.% B by rapid solidification and subsequent heat treatment for 1-20 hrs at 900ºC. High-resolution transmission electron microscopy (HRTEM) characterization showed that primary TiB2 particles were formed in liquid copper. Heat treatment of as-solidified samples led to ...
متن کاملElectro Discharge Machining Of Aluminium Alloy (LM6)-5 wt.% SiCp Composites Using Copper Electrodes
Metal matrix composites (MMCs) are now gaining their usage in aerospace, automotive and biomedical industries because of their inherent properties like high strength to weight ratio, low wear rate etc. To machine these types of materials conventional machining methods are unsuitable because of high tool wear and tooling cost. Electro discharge Machining (EDM) is one of the important nontraditio...
متن کاملThermochemical Heat Storage Properties of Co3O4-X wt % Al2O3 and Co3O4-X wt % Y2O3 Composites (X=1, 2, 5, 8, 10)
The effect of Al2O3 (1-10 wt %) and Y2O3 (1-10 wt %) additions on thermochemical heat storage properties of Co3O4/CoO system was investigated by thermogravimetry, XRD, and SEM analyses. Results showed that the addition of Al2O3 to Co3O4 at constant 8 h mechanical activation improved the...
متن کاملtem characterization and properties of cu-1 wt.% tib2 nanocomposite prepared by rapid solidification and subsequent heat treatment
copper matrix composite reinforced by 1wt.% tib2 particles was prepared using in situ reaction of cu-1.4wt.% ti and cu-0.7wt.% b by rapid solidification and subsequent heat treatment for 1-20 hrs at 900ºc. high-resolution transmission electron microscopy (hrtem) characterization showed that primary tib2 particles were formed in liquid copper. heat treatment of as-solidified samples led to the f...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Platinum Metals Review
سال: 2007
ISSN: 0032-1400,1471-0676
DOI: 10.1595/147106707x187173