Study on the Determination of Fatigue Damage Parameter for Rubber Component under Multiaxial Loading
نویسندگان
چکیده
منابع مشابه
Multiaxial stress effects on fatigue behavior of filled natural rubber
This work explores multiaxial stress effects on fatigue crack nucleation and growth in filled natural rubber based on experiments using short thin-walled cylindrical specimens subjected to axial and twist displacements. Cyclic stress–strain response exhibits significant initial softening relative to the monotonic response, followed by a more gradual additional softening. Irreversible breakage o...
متن کاملCumulative Fatigue Damage Under stepwise Tension-Compression Loading
Rock structures are subjected to cyclic tension-compression loading due to a blasting, earthquake, traffic and injection-production in underground storage case. Therefore study the fatigue behavior of rock samples under this type of loading is required. In this study, the accumulated fatigue damage for a Green Onyx rock sample which consisted of only one mineral composition with two-step high-l...
متن کاملSubstructure Model for Concrete Behavior Simulation under Cyclic Multiaxial Loading
This paper proposes a framework for the constitutive model based on the semi-micromechanical aspects of plasticity, including damage progress for simulating behavior of concrete under multiaxial loading. This model is aimed to be used in plastic and fracture analysis of both regular and reinforced concrete structures, for the framework of sample plane crack approach. This model uses multilamina...
متن کاملInverse first-order reliability method for probabilistic fatigue life prediction of composite laminates under multiaxial loading
Inverse first-order reliability method for probabilistic fatigue life prediction of composite laminates under multiaxial loading Yibing Xiang and Yongming Liu* Department of Civil and Environmental Engineering Clarkson University Potsdam NY.13699, USA Abstract: Multiaxial fatigue reliability is a challenging problem despite extensive progress made during the past few decades. Anisotropic materi...
متن کاملA New Energy-Critical Plane Damage Parameter for Multiaxial Fatigue Life Prediction of Turbine Blades
As one of fracture critical components of an aircraft engine, accurate life prediction of a turbine blade to disk attachment is significant for ensuring the engine structural integrity and reliability. Fatigue failure of a turbine blade is often caused under multiaxial cyclic loadings at high temperatures. In this paper, considering different failure types, a new energy-critical plane damage pa...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Elastomers and Composites
سال: 2012
ISSN: 2092-9676
DOI: 10.7473/ec.2012.47.3.194