Synthesis conditions of nano-sized magnetite powder using reverse coprecipitation method for thermal coagulation therapy
نویسندگان
چکیده
منابع مشابه
Thermal Plasma Synthesis of Nano-sized Powders
Thermal plasmas, normally generated by DC (direct current) arc or inductively coupled RF (Radio Frequency) discharge, can be described as a high enthalpy flame with extremely high temperature fields (1,000~20,000 K) and a wide range of velocity fields from several m/s [1-5] to supersonic values [6-7]. Since the resultant huge enthalpy can be realized for various kinds of plasma forming gases an...
متن کاملsynthesis of amido alkylnaphthols using nano-magnetic particles and surfactants
we used dbsa and nano-magnetic for the synthesis of amido alkylnaphtols.
15 صفحه اولFacile synthesis of nano-sized ZnO by direct precipitation method
In this contribution we are presenting a simple precipitation method to synthesize zinc oxide (ZnO) nanoparticles using zinc nitrate and urea in aqueous solution. The obtained precipitated compound was calcined and structurally characterized by Powder X-ray diffraction (XRD), Thermogravimetric analysis (TGA), Scanning electron microscopy (SEM), Transmission electron microscopy (TEM), Fourier tr...
متن کاملSynthesis of Chromium Oxide Nano Particles by Thermal Decomposition Method
Disclosed is a method of preparing pigmentary chromium oxide nano particles having 50 percent particle size less than about 100 nm. Preparation of nano chromium (III) oxide is investigated by thermal decomposition method. According to the disclosed method, a substantially dry solid composition of potassium dichromate and carbon active is heated in CO2 atmosphere to a temperature of about 60...
متن کاملNew Method for Preparation of Nano Alumina Powder Using Aluminum(III) Complexes by Combustion Synthesis Without Fuel
Alumina nanomaterials were synthesized via a solution combustion technique using tris-(acetylacetonato) aluminum(III) complex (1) and tris-(2-formylphenolate) aluminum(III) complex (2) at 600, and 1000 °C for 3h. The obtained data showed that the procedure without using fuel resulted in a better phase and morphology. To investigate the phase formation, powder X-ray diffraction technique was use...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 2016
ISSN: 1348-6535,1882-0743
DOI: 10.2109/jcersj2.15183